Možnosti cyklické potenciodanymické metody pro stanovení náchylnosti vybraných austenitických ocelí k mezikrystalové korozi.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F07%3A00016239" target="_blank" >RIV/61989100:27360/07:00016239 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Possibility of cyclic potentiodynamic method for the detection of sensitivity of selected stainless steels to intergranular corrosion.

Popis výsledku v původním jazyce

Standard test method for potentiodynamic polarization measurements for localized corrosion susceptibility of Fe-, Ni-, or Co- based alloys (ASTM G61) was applied for the detection and comparison of sensitivity of selected stainless steels to intergranular corrosion. The reduced Cr content or pitting resistance equivalent value at grain boundaries decreases critical pitting temperature, depassivation and repassivation potential values. The parts of polarization curves (like loops, waves) are shifted to the lower potential values and higher current density compared with non-depleted state. The experimental results, including micropitting and etching along grain or phase boundaries, confirmed this approach.

Název v anglickém jazyce

Possibility of cyclic potentiodynamic method for the detection of sensitivity of selected stainless steels to intergranular corrosion.

Popis výsledku anglicky

Standard test method for potentiodynamic polarization measurements for localized corrosion susceptibility of Fe-, Ni-, or Co- based alloys (ASTM G61) was applied for the detection and comparison of sensitivity of selected stainless steels to intergranular corrosion. The reduced Cr content or pitting resistance equivalent value at grain boundaries decreases critical pitting temperature, depassivation and repassivation potential values. The parts of polarization curves (like loops, waves) are shifted to the lower potential values and higher current density compared with non-depleted state. The experimental results, including micropitting and etching along grain or phase boundaries, confirmed this approach.

Druh

D - Stať ve sborníku

CEP obor

JK - Koroze a povrchové úpravy materiálu

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F06%2F1621" target="_blank" >GA106/06/1621: Korozní odolnost pasivního stavu vysokolegovaných materiálů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

1st International Conference Corrosion and Material Protection EFC, 10th Conf. AKI 2007

ISBN

978-80-903933-0-1

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

1-6

Název nakladatele

SVUOM Praha

Místo vydání

Praha 7, U Měšťanského pivovaru

Místo konání akce

—

Datum konání akce

—

Typ akce podle státní příslušnosti

—

Kód UT WoS článku

—