Sulphide Stress Cracking of the Welded Joint from Supermartensitic Steel 13Cr6Ni2,5Mo
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F08%3A00019503" target="_blank" >RIV/61989100:27360/08:00019503 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Sulphide Stress Cracking of the Welded Joint from Supermartensitic Steel 13Cr6Ni2,5Mo
Popis výsledku v původním jazyce
The paper evaluates resistance of the welded joint made of supermartensitic steel 13Cr6Ni2.5Mo to sulfide stress cracking (SSC). None of the tested samples withstood the required values of loading, failure occurred already at very short time intervals. Unsatisfactory resistance can be attributed to high values of mechanical properties of material, which did not sufficiently decrease by tempering, and also to occurrence of undesirable ?-ferrite in structure. In spite of that it was revealed that the welded joint brought even further reduction of resistance to SSC, because the fracture occurred in the samples with welded joint primarily in the weld metal (WM) or in heat affected zone (HAZ) and not in the basic material.
Název v anglickém jazyce
Sulphide Stress Cracking of the Welded Joint from Supermartensitic Steel 13Cr6Ni2,5Mo
Popis výsledku anglicky
The paper evaluates resistance of the welded joint made of supermartensitic steel 13Cr6Ni2.5Mo to sulfide stress cracking (SSC). None of the tested samples withstood the required values of loading, failure occurred already at very short time intervals. Unsatisfactory resistance can be attributed to high values of mechanical properties of material, which did not sufficiently decrease by tempering, and also to occurrence of undesirable ?-ferrite in structure. In spite of that it was revealed that the welded joint brought even further reduction of resistance to SSC, because the fracture occurred in the samples with welded joint primarily in the weld metal (WM) or in heat affected zone (HAZ) and not in the basic material.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2008
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Zeszyty Naukowe, Mechanika
ISBN
—
ISSN
1429-6055
e-ISSN
—
Počet stran výsledku
8
Strana od-do
—
Název nakladatele
Politechnika Opolska
Místo vydání
Opole
Místo konání akce
Jarnoltówek
Datum konání akce
22. 10. 2008
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—