Deformation resistance and structure of a hot-rolled AZ31 magnesium alloy
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F08%3A00019580" target="_blank" >RIV/61989100:27360/08:00019580 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Deformation resistance and structure of a hot-rolled AZ31 magnesium alloy
Popis výsledku v původním jazyce
An experiment leading to obtaining the mathematical model of the mean equivalent stress (MES) of magnesium alloy AZ31 was realized in the laboratory rolling mill. Neglecting of the speed term in the resulting model of MES was possible by a relatively narrow range of applied strain rates, and also by the fact that a close relationship between height strain and strain rate exists. The paper also presents the obtained data, related to the dependencies between deformation process parameters, inhomogeneity and grain size after dynamic recrystallization for the specimens subjected to hot rolling. A significant influence of the deformation temperature on the grain size after recrystallization was identified, while observing lower sensitivity of this parameterto an increased rolling speed.
Název v anglickém jazyce
Deformation resistance and structure of a hot-rolled AZ31 magnesium alloy
Popis výsledku anglicky
An experiment leading to obtaining the mathematical model of the mean equivalent stress (MES) of magnesium alloy AZ31 was realized in the laboratory rolling mill. Neglecting of the speed term in the resulting model of MES was possible by a relatively narrow range of applied strain rates, and also by the fact that a close relationship between height strain and strain rate exists. The paper also presents the obtained data, related to the dependencies between deformation process parameters, inhomogeneity and grain size after dynamic recrystallization for the specimens subjected to hot rolling. A significant influence of the deformation temperature on the grain size after recrystallization was identified, while observing lower sensitivity of this parameterto an increased rolling speed.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2008
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Hutnik, Wiadomości hutnicze
ISSN
1230-3534
e-ISSN
—
Svazek periodika
75
Číslo periodika v rámci svazku
8
Stát vydavatele periodika
PL - Polská republika
Počet stran výsledku
3
Strana od-do
—
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—