Formation of ultra-fine grained structure and mechanical properties by ECAP deformation

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F09%3A00022034" target="_blank" >RIV/61989100:27360/09:00022034 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Formation of ultra-fine grained structure and mechanical properties by ECAP deformation

Popis výsledku v původním jazyce

Commercial pure titanium was deformed by equal channel angular pressing ( ECAP) using up to 8 passes. The evolution of microstructure and fracture character were observed by optical microscopy (OM) and spectral analysis microscopy (SEM). The mean grain size decreased with increasing deformation, after 8 passes to 300 nm. Microscopy analysis suggested the possible ultra-fine structure mechanism by the formation of cellular structure in grains, forming of subgrains and then forming of high angle grains with random orientation. Fractures of ECAP titanium material after 8 passes had transcrystall ductile character with dimple morphology.

Název v anglickém jazyce

Formation of ultra-fine grained structure and mechanical properties by ECAP deformation

Popis výsledku anglicky

Commercial pure titanium was deformed by equal channel angular pressing ( ECAP) using up to 8 passes. The evolution of microstructure and fracture character were observed by optical microscopy (OM) and spectral analysis microscopy (SEM). The mean grain size decreased with increasing deformation, after 8 passes to 300 nm. Microscopy analysis suggested the possible ultra-fine structure mechanism by the formation of cellular structure in grains, forming of subgrains and then forming of high angle grains with random orientation. Fractures of ECAP titanium material after 8 passes had transcrystall ductile character with dimple morphology.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F09%2F1598" target="_blank" >GA106/09/1598: Výzkum vlastností a výroba nanostrukturního titanu pro dentální implantáty</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Rare Metals

ISSN

1001-0521

e-ISSN

—

Svazek periodika

28

Číslo periodika v rámci svazku

special

Stát vydavatele periodika

CN - Čínská lidová republika

Počet stran výsledku

4

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—