Computation of hot forming efficiency

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F09%3A00022369" target="_blank" >RIV/61989100:27360/09:00022369 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Computation of hot forming efficiency

Popis výsledku v původním jazyce

Processing maps on hot rolled 9 Cr steel have been developed in the range 800-1100 °C and 0,1-100 s-1 by plastometric hot plane strain compression test (PSCT) with a view to examine whether the hot workability is efficient. Briefly, the work-piece undergoing hot deformation is considered to be a dissipator of power and the strain rate sensitivity m of flow stress is the factor that partitions power between deformation heat and microstructural changes. The variation of efficiency of power dissipation with temperature and strain rate represents a power dissipation map which is generally viewed as an iso-efficiency contour map. Hot forming behaviour of stainless steel is characterised in processing maps developed on the basis of the Dynamic Materials Model. The material could exhibit a dynamic recrystallization domain in the temperature range of high than 1000 °C or higher and strain rate of 1 s-1.

Název v anglickém jazyce

Computation of hot forming efficiency

Popis výsledku anglicky

Processing maps on hot rolled 9 Cr steel have been developed in the range 800-1100 °C and 0,1-100 s-1 by plastometric hot plane strain compression test (PSCT) with a view to examine whether the hot workability is efficient. Briefly, the work-piece undergoing hot deformation is considered to be a dissipator of power and the strain rate sensitivity m of flow stress is the factor that partitions power between deformation heat and microstructural changes. The variation of efficiency of power dissipation with temperature and strain rate represents a power dissipation map which is generally viewed as an iso-efficiency contour map. Hot forming behaviour of stainless steel is characterised in processing maps developed on the basis of the Dynamic Materials Model. The material could exhibit a dynamic recrystallization domain in the temperature range of high than 1000 °C or higher and strain rate of 1 s-1.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F07%2F0631" target="_blank" >GA106/07/0631: Plastometrická, počítačová a laboratorní simulace uzdravování materiálu tvářeného za tepla</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Sborník vědeckých prací VŠB-TU Ostrava, řada hutnická

ISSN

0474-8484

e-ISSN

—

Svazek periodika

LII

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

6

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—