Characterization of silver nanoparticles deposited on montmorillonite
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F10%3A10224885" target="_blank" >RIV/61989100:27360/10:10224885 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/61388980:_____/10:00358027
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Characterization of silver nanoparticles deposited on montmorillonite
Popis výsledku v původním jazyce
Silver nanoparticles were prepared by reduction of silver ions intercalated into montmorillonite (MMT) with borohydride and formaldehyde. They were deposited on the external surface of the MMT particles. Scanning electron microscopy (SEM), transmission electron microscopy (TEM) and specific surface area (SSA) measurements revealed that borohydride produced very small particles with narrow size distribution (3 - 13 nm) evenly dispersed on the MMT surface. Silver ions reduced by formaldehyde formed both small particles and large aggregates. The Ag nanoparticles were composed of cubic and hexagonal and/or amorphous silver crystals. The Raman scattering (SERS) was significantly increased by montmorillonite covered with Ag nanoparticles, especially when prepared with borohydride.
Název v anglickém jazyce
Characterization of silver nanoparticles deposited on montmorillonite
Popis výsledku anglicky
Silver nanoparticles were prepared by reduction of silver ions intercalated into montmorillonite (MMT) with borohydride and formaldehyde. They were deposited on the external surface of the MMT particles. Scanning electron microscopy (SEM), transmission electron microscopy (TEM) and specific surface area (SSA) measurements revealed that borohydride produced very small particles with narrow size distribution (3 - 13 nm) evenly dispersed on the MMT surface. Silver ions reduced by formaldehyde formed both small particles and large aggregates. The Ag nanoparticles were composed of cubic and hexagonal and/or amorphous silver crystals. The Raman scattering (SERS) was significantly increased by montmorillonite covered with Ag nanoparticles, especially when prepared with borohydride.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/ED0040%2F01%2F01" target="_blank" >ED0040/01/01: Regionální materiálově technologické výzkumné centrum</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)<br>S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Applied Clay Science
ISSN
0169-1317
e-ISSN
—
Svazek periodika
49
Číslo periodika v rámci svazku
3
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
5
Strana od-do
—
Kód UT WoS článku
000280886500037
EID výsledku v databázi Scopus
—