Structural characteristic of Ni3Al alloyed by Zr after directional solidification

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F10%3A86075255" target="_blank" >RIV/61989100:27360/10:86075255 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Structural characteristic of Ni3Al alloyed by Zr after directional solidification

Popis výsledku v původním jazyce

Ni-22Al-2Zr at.% alloy was prepared by induction melting and then directionally re-melted at three different rates, namely, 20, 50 and 70 mm/h. Documenting and analysis of micro-structure and basic investigation of porosity and micro-hardness were carried out on the transversal and longitudinal sections of this alloy.

Název v anglickém jazyce

Structural characteristic of Ni3Al alloyed by Zr after directional solidification

Popis výsledku anglicky

Ni-22Al-2Zr at.% alloy was prepared by induction melting and then directionally re-melted at three different rates, namely, 20, 50 and 70 mm/h. Documenting and analysis of micro-structure and basic investigation of porosity and micro-hardness were carried out on the transversal and longitudinal sections of this alloy.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Den interních doktorandů 2010

ISBN

978-80-248-2344-7

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

—

Název nakladatele

VŠB - TU Ostrava

Místo vydání

Ostrava

Místo konání akce

Ostrava

Datum konání akce

1. 12. 2010

Typ akce podle státní příslušnosti

CST - Celostátní akce

Kód UT WoS článku

—