Structure development in the course of rolling and high-temperature annealing of Fe-Al-Si-C alloy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F10%3A86075791" target="_blank" >RIV/61989100:27360/10:86075791 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Structure development in the course of rolling and high-temperature annealing of Fe-Al-Si-C alloy

Popis výsledku v původním jazyce

A special method of hot rolling of laboratory castings from the alloy Fe ? 29.5 Al ? 0.47 Si ? 1.16 C (wt. %) was developed, preventing the origin of surface cracks in contact with the cold work rolls and enabling forming this material with extremely lowplasticity. This method is based on the application of the welded protective capsules, and the repeated in-process heating of the unfinished rolled product. The structure of the initial castings with thickness 19.5 mm is characterised by a large heterogeneity. After the heating to 1250 °C, the multi-pass hot rolling to the plate of thickness 4.5 mm and the following retarded cooling of the rolled product to temperature 600 °C, the structure with grains sized ca 30 ?m up to 1 mm, stretched in the direction of rolling, was achieved. The long-term annealing of the plate at temperature 1200 °C led progressively to crumbling of the greatest formations and, vice versa, coarsening of the finest grains.

Název v anglickém jazyce

Structure development in the course of rolling and high-temperature annealing of Fe-Al-Si-C alloy

Popis výsledku anglicky

A special method of hot rolling of laboratory castings from the alloy Fe ? 29.5 Al ? 0.47 Si ? 1.16 C (wt. %) was developed, preventing the origin of surface cracks in contact with the cold work rolls and enabling forming this material with extremely lowplasticity. This method is based on the application of the welded protective capsules, and the repeated in-process heating of the unfinished rolled product. The structure of the initial castings with thickness 19.5 mm is characterised by a large heterogeneity. After the heating to 1250 °C, the multi-pass hot rolling to the plate of thickness 4.5 mm and the following retarded cooling of the rolled product to temperature 600 °C, the structure with grains sized ca 30 ?m up to 1 mm, stretched in the direction of rolling, was achieved. The long-term annealing of the plate at temperature 1200 °C led progressively to crumbling of the greatest formations and, vice versa, coarsening of the finest grains.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP107%2F10%2F0438" target="_blank" >GAP107/10/0438: Fyzikální a metalurgické aspekty deformačního chování aluminidů železa s extrémně nízkou plasticitou</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

METAL 2010

ISBN

978-80-87294-17-8

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

322-327

Název nakladatele

Tanger

Místo vydání

Ostrava

Místo konání akce

Hotel Relax, Rožnov pod Radhoštěm

Datum konání akce

18. 5. 2010

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000286658700053