Hot Ductility of Two TRIPLEX Steels

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F11%3A86079284" target="_blank" >RIV/61989100:27360/11:86079284 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61989100:27710/11:86079284

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Hot Ductility of Two TRIPLEX Steels

Popis výsledku v původním jazyce

For two different high manganese steels, with approximately 6 wt. % of aluminium and one with 26 wt. % of manganes (marked as A) and the second with 22 wt. % of manganese (marked as B) in the temperature range of 600°C to 1150°C hot ductility, expressedby reduction of area, was investigated. Determination of stacking fault energy, strength properties and dilatometric measurement of TRIPLEX matrixes completed the hot ductility information. For both steels the deepest troughs were detected between 600°C-800°C which were ascribed to observed AlN particles. The steel A showed the second trough between 900°C-1000°C and the most assumed reason could be the revealed in-homogeneity in form of shrinkage porosities.

Název v anglickém jazyce

Hot Ductility of Two TRIPLEX Steels

Popis výsledku anglicky

For two different high manganese steels, with approximately 6 wt. % of aluminium and one with 26 wt. % of manganes (marked as A) and the second with 22 wt. % of manganese (marked as B) in the temperature range of 600°C to 1150°C hot ductility, expressedby reduction of area, was investigated. Determination of stacking fault energy, strength properties and dilatometric measurement of TRIPLEX matrixes completed the hot ductility information. For both steels the deepest troughs were detected between 600°C-800°C which were ascribed to observed AlN particles. The steel A showed the second trough between 900°C-1000°C and the most assumed reason could be the revealed in-homogeneity in form of shrinkage porosities.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/ED0040%2F01%2F01" target="_blank" >ED0040/01/01: Regionální materiálově technologické výzkumné centrum</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Hutnické listy

ISSN

0018-8069

e-ISSN

—

Svazek periodika

64

Číslo periodika v rámci svazku

6

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

4

Strana od-do

18-21

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—