HSLA 100 steel and its properties upon severe hot deformation

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F11%3A86081055" target="_blank" >RIV/61989100:27360/11:86081055 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

HSLA 100 steel and its properties upon severe hot deformation

Popis výsledku v původním jazyce

Constant demand for quality and excellent mechanical properties of hot-rolled sheet and strip for shipbuilding and for sizable welded tubes for oil and gas pipelines has an impact on the interest in producing HSLA steels. The basic strengthening mechanism in typical HSLA steels depends (apart from the carbon content) on the nature of thermomechanical treatment, the finish-forming temperature and the cooling rate. Selection of the finish-forming temperature should take into account the effects of precipitation hardening which inhibits the recrystallization. It should therefore be below the recrystallization temperature. Forming should end below 800 °C, where heavily deformed austenite transforms into fine ferrite. The steel employed in the experiment had the following chemical composition (wt. %): 0.062 C; 0.75 Mn; 0.77 Si; 0.53 Cu; 3.45 Ni; 0.64 Cr; 0.50 Mo; 0.036 Nb; 0.009 P; 0.0065 S; 0.073 Al. The stock was forged at 1,150°C and converted into 25 x 40 x 500 mm blocks. From these, st

Název v anglickém jazyce

HSLA 100 steel and its properties upon severe hot deformation

Popis výsledku anglicky

Constant demand for quality and excellent mechanical properties of hot-rolled sheet and strip for shipbuilding and for sizable welded tubes for oil and gas pipelines has an impact on the interest in producing HSLA steels. The basic strengthening mechanism in typical HSLA steels depends (apart from the carbon content) on the nature of thermomechanical treatment, the finish-forming temperature and the cooling rate. Selection of the finish-forming temperature should take into account the effects of precipitation hardening which inhibits the recrystallization. It should therefore be below the recrystallization temperature. Forming should end below 800 °C, where heavily deformed austenite transforms into fine ferrite. The steel employed in the experiment had the following chemical composition (wt. %): 0.062 C; 0.75 Mn; 0.77 Si; 0.53 Cu; 3.45 Ni; 0.64 Cr; 0.50 Mo; 0.036 Nb; 0.009 P; 0.0065 S; 0.073 Al. The stock was forged at 1,150°C and converted into 25 x 40 x 500 mm blocks. From these, st

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Hutnické listy

ISSN

0018-8069

e-ISSN

—

Svazek periodika

64

Číslo periodika v rámci svazku

6

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

6

Strana od-do

5-10

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—