Dynamic Recrystallization and Activation Energy at Hot Forming of the Alloy Fe-40Al-Zr-B

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F11%3A86081397" target="_blank" >RIV/61989100:27360/11:86081397 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Dynamic Recrystallization and Activation Energy at Hot Forming of the Alloy Fe-40Al-Zr-B

Popis výsledku v původním jazyce

The fundamental aim was to determine the activation energy of the iron aluminide of the type Fe-40Al-Zr-B. Composition of the studied material in wt.% was 24.4 Al ? 0.17 Mn ? 0.02 C ? 0.17 Zr ? 0.011 B (the remainder is Fe). The aluminium content corresponded to 40.0 at.%. The uniaxial hot compression tests of the cylindrical specimens were performed after the unified preheating to the temperature of 1200°C. The forming temperatures 800 ? 1200°C and the nominal strain rate values 0.05 ? 30 s-1 were chosen. The value of the apparent activation energy Q = 561 kJ x mol-1 in hot forming was calculated. The comparison of this very high value with other results showed an extremely strong strengthening effect of Zr and B in this alloy. Using the obtained value of the activation energy it was possible to derive the useful equations, describing the maximum deformation resistance and the start of the dynamic recrystallization of the investigated material in dependence on temperature and strain r

Název v anglickém jazyce

Dynamic Recrystallization and Activation Energy at Hot Forming of the Alloy Fe-40Al-Zr-B

Popis výsledku anglicky

The fundamental aim was to determine the activation energy of the iron aluminide of the type Fe-40Al-Zr-B. Composition of the studied material in wt.% was 24.4 Al ? 0.17 Mn ? 0.02 C ? 0.17 Zr ? 0.011 B (the remainder is Fe). The aluminium content corresponded to 40.0 at.%. The uniaxial hot compression tests of the cylindrical specimens were performed after the unified preheating to the temperature of 1200°C. The forming temperatures 800 ? 1200°C and the nominal strain rate values 0.05 ? 30 s-1 were chosen. The value of the apparent activation energy Q = 561 kJ x mol-1 in hot forming was calculated. The comparison of this very high value with other results showed an extremely strong strengthening effect of Zr and B in this alloy. Using the obtained value of the activation energy it was possible to derive the useful equations, describing the maximum deformation resistance and the start of the dynamic recrystallization of the investigated material in dependence on temperature and strain r

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP107%2F10%2F0438" target="_blank" >GAP107/10/0438: Fyzikální a metalurgické aspekty deformačního chování aluminidů železa s extrémně nízkou plasticitou</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Hutnické listy

ISSN

0018-8069

e-ISSN

—

Svazek periodika

64

Číslo periodika v rámci svazku

6

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

4

Strana od-do

62-65

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—