Influence of thermal expansion in the utilization of hybrid sands

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F11%3A86081657" target="_blank" >RIV/61989100:27360/11:86081657 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Influence of thermal expansion in the utilization of hybrid sands

Popis výsledku v původním jazyce

Nowadays, it is important that foundries casting production will prove minimum production costs with ensuring the highest possible quality. Primarily this is related to elimination of products defects. One of the main causes of defects is the thermal dilatation of the sands in the molding mixtures. Usually used quartz sands demonstrated discontinuous (no-flowing) thermal expansion which is related to dimensional inaccuracies due to changes in modification of SiO2. Dilatation coefficient reports the dimensional changes after heat exposure. The high values of this coefficient define the utilization of this material for the production of thin-walled and very accurate castings. Thermal expansion of molding mixture is determined by dilatometric method, which records linear changes during analysis time. The result of this measurement is the dilatometric curve. Purity, shape, angularity, grain size, bulk density and micro-dilatation of individual grains influence dilatometric values of sands,

Název v anglickém jazyce

Influence of thermal expansion in the utilization of hybrid sands

Popis výsledku anglicky

Nowadays, it is important that foundries casting production will prove minimum production costs with ensuring the highest possible quality. Primarily this is related to elimination of products defects. One of the main causes of defects is the thermal dilatation of the sands in the molding mixtures. Usually used quartz sands demonstrated discontinuous (no-flowing) thermal expansion which is related to dimensional inaccuracies due to changes in modification of SiO2. Dilatation coefficient reports the dimensional changes after heat exposure. The high values of this coefficient define the utilization of this material for the production of thin-walled and very accurate castings. Thermal expansion of molding mixture is determined by dilatometric method, which records linear changes during analysis time. The result of this measurement is the dilatometric curve. Purity, shape, angularity, grain size, bulk density and micro-dilatation of individual grains influence dilatometric values of sands,

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Den interních doktorandů 2011 : sborník semináře Fakulty metalurgie a materiálového inženýrství : Vysoká škola báňská - Technická univerzita Ostrava, 6.12.2011

ISBN

978-80-248-2523-6

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

15-18

Název nakladatele

Vysoká škola báňská - Technická univerzita Ostrava, Fakulta metalurgie a materiálového inženýrství

Místo vydání

Ostrava

Místo konání akce

Ostrava

Datum konání akce

6. 12. 2011

Typ akce podle státní příslušnosti

CST - Celostátní akce

Kód UT WoS článku

—