Control of microstructure of cast irons Indefinite Chill Double Pour- ICDP

Popis výsledku v původním jazyce

ICDP cast irons designated for working layer of centrifugal cylinders of rolling mill must have precisely defined properties. The most closely observed parameters of the ICDP (Indefinite Child Double Pour) cast irons are the following: the amount of graphite in a microstructure and hardness of base metal material. Secretion of graphite in cast iron with ledeburitic basic metal compound is a complex process that can be controlled and managed with the use of thermal analysis. On the basis of the evaluation of cooling curve parameters of cast iron there is performed metallurgical adjustment of meltage by adding elements supporting graphite end carbide formation into cast iron. The identified structural and mechanical properties of ICDP cast irons were correlated with recorded KO. Subsequently, a methodology for control of the metallurgical adjustment of cast iron before casting was proposed so as to ensure the desired microstructure and properties the ICDP cast iron.

Název v anglickém jazyce

Control of microstructure of cast irons Indefinite Chill Double Pour- ICDP

Popis výsledku anglicky

ICDP cast irons designated for working layer of centrifugal cylinders of rolling mill must have precisely defined properties. The most closely observed parameters of the ICDP (Indefinite Child Double Pour) cast irons are the following: the amount of graphite in a microstructure and hardness of base metal material. Secretion of graphite in cast iron with ledeburitic basic metal compound is a complex process that can be controlled and managed with the use of thermal analysis. On the basis of the evaluation of cooling curve parameters of cast iron there is performed metallurgical adjustment of meltage by adding elements supporting graphite end carbide formation into cast iron. The identified structural and mechanical properties of ICDP cast irons were correlated with recorded KO. Subsequently, a methodology for control of the metallurgical adjustment of cast iron before casting was proposed so as to ensure the desired microstructure and properties the ICDP cast iron.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/FR-TI2%2F188" target="_blank" >FR-TI2/188: *Výzkum a vývoj materiálů pracovních vrstev odstředivě litých vícevrstvých válců orientovaný na moderní trendy válcovacích tratí.</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

ARCHIVES of FOUNDRY ENGINEERING

ISSN

1897-3310

e-ISSN

—

Svazek periodika

11

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

PL - Polská republika

Počet stran výsledku

5

Strana od-do

199-203

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—