Effect of calcination temperature and calcination time on the kaolinite/TiO2 composite for photocatalytic reduction of CO2

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F12%3A86083623" target="_blank" >RIV/61989100:27360/12:86083623 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Effect of calcination temperature and calcination time on the kaolinite/TiO2 composite for photocatalytic reduction of CO2

Popis výsledku v původním jazyce

The kaolinite/TiO2 composite (60 wt% of TiO2) was prepared by thermal hydrolysis of a raw kaolin suspension in titanyl sulphate and calcined at different temperatures (600, 650 and 700°C) and for different times (1, 2 and 3 h). The obtained samples werecharacterized by XRPD, N2 physical adsorption and SEM, and tested for photocatalytic reduction of CO2. The different calcination conditions did not influence TiO2 phase composition, only slightly changed the specific surface area, and significantly affected crystallite size of kaolinite/TiO2 composite. A higher temperature and longer duration of calcination lead to higher crystallinity of the powder. The photocatalytic results showed that the crystallite size determined the efficiency of kaolinite/TiO2photocatalysts.

Název v anglickém jazyce

Effect of calcination temperature and calcination time on the kaolinite/TiO2 composite for photocatalytic reduction of CO2

Popis výsledku anglicky

The kaolinite/TiO2 composite (60 wt% of TiO2) was prepared by thermal hydrolysis of a raw kaolin suspension in titanyl sulphate and calcined at different temperatures (600, 650 and 700°C) and for different times (1, 2 and 3 h). The obtained samples werecharacterized by XRPD, N2 physical adsorption and SEM, and tested for photocatalytic reduction of CO2. The different calcination conditions did not influence TiO2 phase composition, only slightly changed the specific surface area, and significantly affected crystallite size of kaolinite/TiO2 composite. A higher temperature and longer duration of calcination lead to higher crystallinity of the powder. The photocatalytic results showed that the crystallite size determined the efficiency of kaolinite/TiO2photocatalysts.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CI - Průmyslová chemie a chemické inženýrství

OECD FORD obor

—

Projekt

<a href="/cs/project/ED2.1.00%2F03.0069" target="_blank" >ED2.1.00/03.0069: ENET - Energetické jednotky pro využití netradičních zdrojů energie</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

GeoScience Engineering

ISSN

1802-5420

e-ISSN

—

Svazek periodika

58

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

13

Strana od-do

10-22

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—