HYDROGEN INDUCED CRACKING OF Ti CLAD TO THE 304 SS IN ANNEALED STATE
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F12%3A86083839" target="_blank" >RIV/61989100:27360/12:86083839 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/61989100:27360/13:86088303
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
HYDROGEN INDUCED CRACKING OF Ti CLAD TO THE 304 SS IN ANNEALED STATE
Popis výsledku v původním jazyce
Hydrogen induced cracking of Ti clad to the 304 SS in annealed state after explosive welding was investigated. The total crack sensitivity ratio (CSR), crack length one (CLR) and crack thickness ratio (CTR) according the NACE Standard TM0284 item No. 21215 were evaluated. The results were confronted with the 5L ANSI/API Specification valid for country tubular goods. Results were discussed on the basis of metallographic evaluation of the weld interface and its close neighbourhood. Numerous short and thick cracks were detected in materials of both processing types. After heat treatment, bimetal showed lower cracks count. Generally, the cracks were situated in the vicinity of bonding line of weld in intermetallic phases.
Název v anglickém jazyce
HYDROGEN INDUCED CRACKING OF Ti CLAD TO THE 304 SS IN ANNEALED STATE
Popis výsledku anglicky
Hydrogen induced cracking of Ti clad to the 304 SS in annealed state after explosive welding was investigated. The total crack sensitivity ratio (CSR), crack length one (CLR) and crack thickness ratio (CTR) according the NACE Standard TM0284 item No. 21215 were evaluated. The results were confronted with the 5L ANSI/API Specification valid for country tubular goods. Results were discussed on the basis of metallographic evaluation of the weld interface and its close neighbourhood. Numerous short and thick cracks were detected in materials of both processing types. After heat treatment, bimetal showed lower cracks count. Generally, the cracks were situated in the vicinity of bonding line of weld in intermetallic phases.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/ED0040%2F01%2F01" target="_blank" >ED0040/01/01: Regionální materiálově technologické výzkumné centrum</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2013
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
METAL 2012 : 21st International Conference on Metallurgy and Materials : conference proceedings
ISBN
978-80-87294-31-4
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
589-594
Název nakladatele
Tanger
Místo vydání
Ostrava
Místo konání akce
Brno
Datum konání akce
23. 5. 2012
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—