Microstructure characteristics of Ni3Al based intermetallic compounds

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F12%3A86084243" target="_blank" >RIV/61989100:27360/12:86084243 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Microstructure characteristics of Ni3Al based intermetallic compounds
Popis výsledku v původním jazyce
Microstructure Characteristics of Ni3Al Based Intermetallic Compounds Observations were made in orientated state of non-alloyed intermetallic Ni3Al based compound (22-25 at.% of Al). The samples were solidified by Bridgman's technique. It was establishedthat Ni22Al samples contained formations of Ni3Al (gamma') and solid solution of nickel (gamma), Ni25Al samples contained Ni3Al only. The differences of mechanical properties were not manifested at measurement of micro-hardness, which is for all the samples approximately within the interval from 240 to 260 HV 0.05.
Název v anglickém jazyce
Microstructure characteristics of Ni3Al based intermetallic compounds
Popis výsledku anglicky
Microstructure Characteristics of Ni3Al Based Intermetallic Compounds Observations were made in orientated state of non-alloyed intermetallic Ni3Al based compound (22-25 at.% of Al). The samples were solidified by Bridgman's technique. It was establishedthat Ni22Al samples contained formations of Ni3Al (gamma') and solid solution of nickel (gamma), Ni25Al samples contained Ni3Al only. The differences of mechanical properties were not manifested at measurement of micro-hardness, which is for all the samples approximately within the interval from 240 to 260 HV 0.05.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—

Rok uplatnění
2012
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)