Structural changes of single crystals of low-alloyed tungsten alloys at thermal cycling
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F12%3A86084259" target="_blank" >RIV/61989100:27360/12:86084259 - isvavai.cz</a>
Výsledek na webu
<a href="http://80.www.sciencedirect.com.dialog.cvut.cz/science/article/pii/S0263436812000224" target="_blank" >http://80.www.sciencedirect.com.dialog.cvut.cz/science/article/pii/S0263436812000224</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.ijrmhm.2012.02.001" target="_blank" >10.1016/j.ijrmhm.2012.02.001</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Structural changes of single crystals of low-alloyed tungsten alloys at thermal cycling
Popis výsledku v původním jazyce
Parameters of sub-structure of single crystals of low-alloyed tungsten alloys from the system W-Nb and W-Mo were investigated after thermal cycling in argon protective atmosphere. The mode of thermal cycling of tungsten based single crystals consisted ofheating to the temperature of 2500 degrees C and of cooling to the temperature of 500 degrees C with dwell of 3.5 s at those temperature. It was established with use of X-ray topography, OLM and SEM, that after 100 thermocycles dislocations were re-distributed, sub-boundaries of the 2nd order were "washed away" (disappeared), and the size of sub-grains of the 1st order and their angle disorientations increased - as a result of heat stresses. After 500 thermocycles formation of new boundaries was observed in the structure as a result of polygonisation, i.e. by ordering of dislocations of the same sign. Application of 2000 thermocycles led to an increase of size of new grains and that of their angle disorientations. All the tested sample
Název v anglickém jazyce
Structural changes of single crystals of low-alloyed tungsten alloys at thermal cycling
Popis výsledku anglicky
Parameters of sub-structure of single crystals of low-alloyed tungsten alloys from the system W-Nb and W-Mo were investigated after thermal cycling in argon protective atmosphere. The mode of thermal cycling of tungsten based single crystals consisted ofheating to the temperature of 2500 degrees C and of cooling to the temperature of 500 degrees C with dwell of 3.5 s at those temperature. It was established with use of X-ray topography, OLM and SEM, that after 100 thermocycles dislocations were re-distributed, sub-boundaries of the 2nd order were "washed away" (disappeared), and the size of sub-grains of the 1st order and their angle disorientations increased - as a result of heat stresses. After 500 thermocycles formation of new boundaries was observed in the structure as a result of polygonisation, i.e. by ordering of dislocations of the same sign. Application of 2000 thermocycles led to an increase of size of new grains and that of their angle disorientations. All the tested sample
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2012
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
International Journal of Refractory Metals and Hard Materials
ISSN
0263-4368
e-ISSN
—
Svazek periodika
32
Číslo periodika v rámci svazku
neuveden
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
5
Strana od-do
61-65
Kód UT WoS článku
000302841400011
EID výsledku v databázi Scopus
—