Phenomenological model of hot deformation resistance of the C-Mn-V-B-type HSLA steel

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F12%3A86084484" target="_blank" >RIV/61989100:27360/12:86084484 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Phenomenological model of hot deformation resistance of the C-Mn-V-B-type HSLA steel

Popis výsledku v původním jazyce

Based on the measurement of roll forces during the laboratory rolling of flat samples graded in thickness, new hot mean flow stress model of the HSLA steel of the type C-Mn-V-B was developed. It describes with a very good accuracy the mean flow stress min the temperature range T = 850 ? 1190 degree C, effective height reductions up to eh = 0.66, and strain rates in the range of ? = 8 ? 103 s-1. The newly proposed model solves by phenomenological means a frequent problem with heteroscedasticity of relative deviations between the calculated and experimental values of deformation resistance in the case of the temperature effect. Mean flow stress values of steel C-Mn-V-B were compared with the formerly obtained m values for steels of type C-Mn as well asC-Mn-Nb-V. It was proved that HSLA steel with V and B displayed relatively very low deformation resistance and a minimum strain sensitivity at hot forming.

Název v anglickém jazyce

Phenomenological model of hot deformation resistance of the C-Mn-V-B-type HSLA steel

Popis výsledku anglicky

Based on the measurement of roll forces during the laboratory rolling of flat samples graded in thickness, new hot mean flow stress model of the HSLA steel of the type C-Mn-V-B was developed. It describes with a very good accuracy the mean flow stress min the temperature range T = 850 ? 1190 degree C, effective height reductions up to eh = 0.66, and strain rates in the range of ? = 8 ? 103 s-1. The newly proposed model solves by phenomenological means a frequent problem with heteroscedasticity of relative deviations between the calculated and experimental values of deformation resistance in the case of the temperature effect. Mean flow stress values of steel C-Mn-V-B were compared with the formerly obtained m values for steels of type C-Mn as well asC-Mn-Nb-V. It was proved that HSLA steel with V and B displayed relatively very low deformation resistance and a minimum strain sensitivity at hot forming.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

METAL 2012 : 21st International Conference on Metallurgy and Materials : conference proceedings

ISBN

978-80-87294-31-4

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

264-269

Název nakladatele

Tanger

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

23. 5. 2012

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—