CRACKING OF PISTOLS BARRELS

Popis výsledku v původním jazyce

Pistols are unique products with reference to their using. The safety is in this problem important factor also in case of sporting arms. A pistol barrel is one of more stressed construction parts. In consequence is important carefully studying its longevity. This paper deals and analyse possible reasons of cracking of concrete pistol barrels. Fatigue damage is occurred on these samples in gate area. The fracture initiate in section where the gunlock clip hold pistol barrel in gun frame. Two gun-barrel materials were compared. The steel 32CrMoV12-10 holds much lower shots than in the event material 34CrMoNi6. Hardness measurement, metallographic observations, electron microscopy documentation of fracture surfaces and GDS analysis of chemical compositionfor solution to this problem were used. Low cycle fatigue processes proving as source of this problem.

Název v anglickém jazyce

CRACKING OF PISTOLS BARRELS

Popis výsledku anglicky

Pistols are unique products with reference to their using. The safety is in this problem important factor also in case of sporting arms. A pistol barrel is one of more stressed construction parts. In consequence is important carefully studying its longevity. This paper deals and analyse possible reasons of cracking of concrete pistol barrels. Fatigue damage is occurred on these samples in gate area. The fracture initiate in section where the gunlock clip hold pistol barrel in gun frame. Two gun-barrel materials were compared. The steel 32CrMoV12-10 holds much lower shots than in the event material 34CrMoNi6. Hardness measurement, metallographic observations, electron microscopy documentation of fracture surfaces and GDS analysis of chemical compositionfor solution to this problem were used. Low cycle fatigue processes proving as source of this problem.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/ED0040%2F01%2F01" target="_blank" >ED0040/01/01: Regionální materiálově technologické výzkumné centrum</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

New methods of damage and failure analysis of structural parts : [proceedings of the grant workshop on ... : Technical University of Ostrava, Czech Republic, 10.-14.9.2012]

ISBN

978-80-248-2802-2

ISSN

—

e-ISSN

—

Počet stran výsledku

7

Strana od-do

321 - 327

Název nakladatele

VŠB - Technická univerzita Ostrava

Místo vydání

Ostrava

Místo konání akce

Ostrava

Datum konání akce

10. 9. 2012

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—