The Influence of Testing Methodology and Changes of Microstructural Parameters on Resistance of Duplex Steel to Sulphide Stress Cracking
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F13%3A86087397" target="_blank" >RIV/61989100:27360/13:86087397 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/25870807:_____/13:#0000334
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The Influence of Testing Methodology and Changes of Microstructural Parameters on Resistance of Duplex Steel to Sulphide Stress Cracking
Popis výsledku v původním jazyce
The paper is focused on the evaluation of duplex ferritic-austenitic steel resistance to sulphide stress cracking (SSC). The testing was performed in accordance with the NACE TM 0177 Standard using tensile tests and four-point bending tests. The steel was always tested in two different structural states, in the as-received state (marked as AR), and after laboratory annealing by the mode of 800oC/5h/air (marked as AN). Microstructure of steel in the AR state was formed by ferrite and austenite, the AN state was characterized by an disintegration of the part of ferrite and by formation of brittle ? phase. The aim of this study was to evaluate the effect of testing methodologies and changes of microstructural parameters of duplex steel resistance to SSC.
Název v anglickém jazyce
The Influence of Testing Methodology and Changes of Microstructural Parameters on Resistance of Duplex Steel to Sulphide Stress Cracking
Popis výsledku anglicky
The paper is focused on the evaluation of duplex ferritic-austenitic steel resistance to sulphide stress cracking (SSC). The testing was performed in accordance with the NACE TM 0177 Standard using tensile tests and four-point bending tests. The steel was always tested in two different structural states, in the as-received state (marked as AR), and after laboratory annealing by the mode of 800oC/5h/air (marked as AN). Microstructure of steel in the AR state was formed by ferrite and austenite, the AN state was characterized by an disintegration of the part of ferrite and by formation of brittle ? phase. The aim of this study was to evaluate the effect of testing methodologies and changes of microstructural parameters of duplex steel resistance to SSC.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/ED0040%2F01%2F01" target="_blank" >ED0040/01/01: Regionální materiálově technologické výzkumné centrum</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2013
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Metalurgija = Metallurgy
ISSN
0543-5846
e-ISSN
—
Svazek periodika
52
Číslo periodika v rámci svazku
3
Stát vydavatele periodika
HR - Chorvatská republika
Počet stran výsledku
4
Strana od-do
313-316
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—