Analysis of Atypical Breakout During Radial Continuous Casting of Slab in the Straightening Zone II. Analysis of the Causes of the Breakout by Application of the Theory of Physical Similarity

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F13%3A86088076" target="_blank" >RIV/61989100:27360/13:86088076 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Analysis of Atypical Breakout During Radial Continuous Casting of Slab in the Straightening Zone II. Analysis of the Causes of the Breakout by Application of the Theory of Physical Similarity

Popis výsledku v původním jazyce

The so called secondary cooling zone, which is divided into thirteen sections, is an important part of the CCM. In this zone, specifically in the area of the beginning of slab straightening, a breakout may occur due to an increase of the local and temperature heterogeneity of steel, resulting from an increase of the stress caused by bending of the slab and by high local concentration of non-metalic slag inclusions. In the event that two melts are cast one right after another, i.e. if the melt of steel with chemical composition A ends and it is immediately followed by the steel B, it may automatically stop the CCM and an atypical breakout may take place. It happened during continuous casting of the slab 250x1530 mm in the area of straightening. With useof dimensional analysis altogether 8 criteria of similarity were derived according to the ?-theorem. Table of 12 technological, geometrical and thermo-physical dimensional quantities was compiled for these criteria, which characterise bo

Název v anglickém jazyce

Analysis of Atypical Breakout During Radial Continuous Casting of Slab in the Straightening Zone II. Analysis of the Causes of the Breakout by Application of the Theory of Physical Similarity

Popis výsledku anglicky

The so called secondary cooling zone, which is divided into thirteen sections, is an important part of the CCM. In this zone, specifically in the area of the beginning of slab straightening, a breakout may occur due to an increase of the local and temperature heterogeneity of steel, resulting from an increase of the stress caused by bending of the slab and by high local concentration of non-metalic slag inclusions. In the event that two melts are cast one right after another, i.e. if the melt of steel with chemical composition A ends and it is immediately followed by the steel B, it may automatically stop the CCM and an atypical breakout may take place. It happened during continuous casting of the slab 250x1530 mm in the area of straightening. With useof dimensional analysis altogether 8 criteria of similarity were derived according to the ?-theorem. Table of 12 technological, geometrical and thermo-physical dimensional quantities was compiled for these criteria, which characterise bo

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP107%2F11%2F1566" target="_blank" >GAP107/11/1566: Analýza vlivu metalurgicko-materiálových a technologických parametrů kontinuálně litých ocelových předlitků na jejich kvalitu a na stabilitu pochodu</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Hutnické listy

ISSN

0018-8069

e-ISSN

—

Svazek periodika

66

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

9

Strana od-do

17-25

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—