CORROSION BEHAVIOUR OF SELECTED HIGH MANGANESE AUSTENITIC STEELS
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F13%3A86089163" target="_blank" >RIV/61989100:27360/13:86089163 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/61989100:27360/14:86091232
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
CORROSION BEHAVIOUR OF SELECTED HIGH MANGANESE AUSTENITIC STEELS
Popis výsledku v původním jazyce
High-manganese steels (20-30% Mn, suitable for cars) have higher toughness and ductility compared to unalloyed structural steels at comparable strength properties. The corrosion resistance of these steels can be reduced by a high content of manganese which is not electrochemically noble element. In this paper are compared the results of corrosion tests of TWIP (X70Mn22) and TRIPLEX (X100MnAl28-12) steels in rolled and annealed state with structural carbon steel C17 (CSN 411375). The cyclic potentiodynamic method for pitting sensitivity in neutral NaCl solution and potentiodynamic polarization method for assessing the resistance to uniform corrosion in acidic conditions (sulfuric acid water solution) were used. Exposition standard salt spray test, gravimetric method as well as microscopic observations of structure and corrosion were also applied. Based on the exposure tests and measurements the average corrosion rates (non-uniform and pitting) were determined and the ranking of steel re
Název v anglickém jazyce
CORROSION BEHAVIOUR OF SELECTED HIGH MANGANESE AUSTENITIC STEELS
Popis výsledku anglicky
High-manganese steels (20-30% Mn, suitable for cars) have higher toughness and ductility compared to unalloyed structural steels at comparable strength properties. The corrosion resistance of these steels can be reduced by a high content of manganese which is not electrochemically noble element. In this paper are compared the results of corrosion tests of TWIP (X70Mn22) and TRIPLEX (X100MnAl28-12) steels in rolled and annealed state with structural carbon steel C17 (CSN 411375). The cyclic potentiodynamic method for pitting sensitivity in neutral NaCl solution and potentiodynamic polarization method for assessing the resistance to uniform corrosion in acidic conditions (sulfuric acid water solution) were used. Exposition standard salt spray test, gravimetric method as well as microscopic observations of structure and corrosion were also applied. Based on the exposure tests and measurements the average corrosion rates (non-uniform and pitting) were determined and the ranking of steel re
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JK - Koroze a povrchové úpravy materiálu
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/ED0040%2F01%2F01" target="_blank" >ED0040/01/01: Regionální materiálově technologické výzkumné centrum</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
METAL 2013 : 22nd International Conference on Metallurgy and Materials : conference proceedings : May 15th - 17th 2013, Hotel Voronez I, Brno Czech Republic, EU [CD-ROM]
ISBN
978-80-87294-41-3
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
1-6
Název nakladatele
Tanger
Místo vydání
Ostrava
Místo konání akce
Brno
Datum konání akce
15. 5. 2013
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—