Evaluation of Materials Degradation Extent after their Long Term Exposition in Power Plants Equipments
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F14%3A86089234" target="_blank" >RIV/61989100:27360/14:86089234 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.4028/www.scientific.net/MSF.782.325" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/MSF.782.325</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/MSF.782.325" target="_blank" >10.4028/www.scientific.net/MSF.782.325</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Evaluation of Materials Degradation Extent after their Long Term Exposition in Power Plants Equipments
Popis výsledku v původním jazyce
Load processes and their interaction over long-term service exposition influence on degradation of construction materials in the equipment of conventional power plants. A wide range of destructive testing methods and number of tests for each of them wereused to clarify of the extent and mechanism of the damage steel components of the power plants pressure circuit. Changes of material properties were by those methods evaluated in state after operational exposition - till 190 000 hours and after heat treatment reprocessing, for all observed components in the entire profile of the wall thickness. Great attention was paid to metallographic evaluation of the creep damage also. The results of tests were compared with the supposed properties of the undegraded material in origin state.
Název v anglickém jazyce
Evaluation of Materials Degradation Extent after their Long Term Exposition in Power Plants Equipments
Popis výsledku anglicky
Load processes and their interaction over long-term service exposition influence on degradation of construction materials in the equipment of conventional power plants. A wide range of destructive testing methods and number of tests for each of them wereused to clarify of the extent and mechanism of the damage steel components of the power plants pressure circuit. Changes of material properties were by those methods evaluated in state after operational exposition - till 190 000 hours and after heat treatment reprocessing, for all observed components in the entire profile of the wall thickness. Great attention was paid to metallographic evaluation of the creep damage also. The results of tests were compared with the supposed properties of the undegraded material in origin state.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/LO1203" target="_blank" >LO1203: Regionální materiálově technologické výzkumné centrum - Program udržitelnosti</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Materials Science Forum
ISSN
0255-5476
e-ISSN
—
Svazek periodika
782
Číslo periodika v rámci svazku
Metalography XV
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
6
Strana od-do
325-330
Kód UT WoS článku
000338978600058
EID výsledku v databázi Scopus
—