PHASE ANALYSIS EXPLOSIVE WELDED Ti-Cr/Ni STEEL IN AS-RECEIVED STATE AND AFTER HEAT TREATMENT USING SYNCHROTRON
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F14%3A86091220" target="_blank" >RIV/61989100:27360/14:86091220 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
PHASE ANALYSIS EXPLOSIVE WELDED Ti-Cr/Ni STEEL IN AS-RECEIVED STATE AND AFTER HEAT TREATMENT USING SYNCHROTRON
Popis výsledku v původním jazyce
Surface coatings protection is one of the most important processes of treatment. One type of surface coating is explosive bonding. At interface of clad and basic material intermetallic phases are formed, representing quite different matrix with dissimilar properties unlike the welded materials. The work is focused on interface shape line, inhomogeneities in vicinity of the wave joint both in basic material and in vicinity of weld line of the Ti and Cr/Ni stainless steel (SS) matrix. Investigated weld was both in as-received state and after heat treatment carried out at 600°C/90 minutes/air. Presented phases have been identified using X-ray diffraction performed by synchrotron. The Ti-?, Fe-fcc, Fe-bcc and intermetallic phases Fe2Ti were detected at interface area.
Název v anglickém jazyce
PHASE ANALYSIS EXPLOSIVE WELDED Ti-Cr/Ni STEEL IN AS-RECEIVED STATE AND AFTER HEAT TREATMENT USING SYNCHROTRON
Popis výsledku anglicky
Surface coatings protection is one of the most important processes of treatment. One type of surface coating is explosive bonding. At interface of clad and basic material intermetallic phases are formed, representing quite different matrix with dissimilar properties unlike the welded materials. The work is focused on interface shape line, inhomogeneities in vicinity of the wave joint both in basic material and in vicinity of weld line of the Ti and Cr/Ni stainless steel (SS) matrix. Investigated weld was both in as-received state and after heat treatment carried out at 600°C/90 minutes/air. Presented phases have been identified using X-ray diffraction performed by synchrotron. The Ti-?, Fe-fcc, Fe-bcc and intermetallic phases Fe2Ti were detected at interface area.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/LO1203" target="_blank" >LO1203: Regionální materiálově technologické výzkumné centrum - Program udržitelnosti</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Archives of Metallurgy and Materials
ISSN
1733-3490
e-ISSN
—
Svazek periodika
59
Číslo periodika v rámci svazku
4
Stát vydavatele periodika
PL - Polská republika
Počet stran výsledku
4
Strana od-do
1611-1614
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—