Structural variability of high purity cordierite/steatite ceramics sintered from mixtures with various vermiculites
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F14%3A86092025" target="_blank" >RIV/61989100:27360/14:86092025 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/61989100:27740/14:86092025 RIV/61989100:27640/14:86092025
Výsledek na webu
<a href="http://www.sciencedirect.com/science/article/pii/S027288421400087X" target="_blank" >http://www.sciencedirect.com/science/article/pii/S027288421400087X</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.ceramint.2014.01.060" target="_blank" >10.1016/j.ceramint.2014.01.060</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Structural variability of high purity cordierite/steatite ceramics sintered from mixtures with various vermiculites
Popis výsledku v původním jazyce
The cordierite/steatite ceramics were prepared from the pre-ceramic clay mineral mixtures containing talc, kaolinite and unconventionally used vermiculite. Mixtures were sintered in crucibles and in pressed pellets. Quantitative X-ray diffraction phase analysis revealed approximately a 5 vol% lower content of indialite sintered in pellets than in crucibles, and protoenstatite slightly prevailing over orthoenstatite at all ceramic samples. Ceramic samples showed linear dependency of porosity on the increasing content of potassium and sodium in structure of vermiculites. Highest porosity, 55%, was detected for sample in crucible made of vermiculite admixture from Letovice region (CR) and the smallest porosity, 0.25%, was in a sample in pellets made of vermiculite admixture from the Xinlong deposit (China).
Název v anglickém jazyce
Structural variability of high purity cordierite/steatite ceramics sintered from mixtures with various vermiculites
Popis výsledku anglicky
The cordierite/steatite ceramics were prepared from the pre-ceramic clay mineral mixtures containing talc, kaolinite and unconventionally used vermiculite. Mixtures were sintered in crucibles and in pressed pellets. Quantitative X-ray diffraction phase analysis revealed approximately a 5 vol% lower content of indialite sintered in pellets than in crucibles, and protoenstatite slightly prevailing over orthoenstatite at all ceramic samples. Ceramic samples showed linear dependency of porosity on the increasing content of potassium and sodium in structure of vermiculites. Highest porosity, 55%, was detected for sample in crucible made of vermiculite admixture from Letovice region (CR) and the smallest porosity, 0.25%, was in a sample in pellets made of vermiculite admixture from the Xinlong deposit (China).
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
DB - Geologie a mineralogie
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Ceramics International
ISSN
0272-8842
e-ISSN
—
Svazek periodika
40
Číslo periodika v rámci svazku
6
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
10
Strana od-do
8489-8498
Kód UT WoS článku
000335201800105
EID výsledku v databázi Scopus
—