Contribution to the Thermal Properties of Selected Steels

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F15%3A86091371" target="_blank" >RIV/61989100:27360/15:86091371 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/25870807:_____/15:#0000421

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Contribution to the Thermal Properties of Selected Steels

Popis výsledku v původním jazyce

The paper deals with the influence of structural changes on heat transport phenomena of steels samples. Three samples of 10GN2MFA steel were thermally treated at quenching temperatures equal to 900 oC, 1 000 oC and 1 100 oC, and temperature of the tempering was 670 oC. Both thermal diffusivity and thermal conductivity increase with the quenching temperature. Specific heat capacity of steel samples after thermal treatment does not change significantly. Further three different high manganese steels were measured. Maximal content of Mn and C was 27 and 0,5 mass percent. From results of thermophysical properties after ageing, one can see the increase of thermal diffusivity up to 20 percent, thermal conductivity up to 15 percent, decrease of specific heat capacity is not significant. All measured values of thermophysical properties are in good agreement with literary data (before ageing).

Název v anglickém jazyce

Contribution to the Thermal Properties of Selected Steels

Popis výsledku anglicky

The paper deals with the influence of structural changes on heat transport phenomena of steels samples. Three samples of 10GN2MFA steel were thermally treated at quenching temperatures equal to 900 oC, 1 000 oC and 1 100 oC, and temperature of the tempering was 670 oC. Both thermal diffusivity and thermal conductivity increase with the quenching temperature. Specific heat capacity of steel samples after thermal treatment does not change significantly. Further three different high manganese steels were measured. Maximal content of Mn and C was 27 and 0,5 mass percent. From results of thermophysical properties after ageing, one can see the increase of thermal diffusivity up to 20 percent, thermal conductivity up to 15 percent, decrease of specific heat capacity is not significant. All measured values of thermophysical properties are in good agreement with literary data (before ageing).

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/LO1203" target="_blank" >LO1203: Regionální materiálově technologické výzkumné centrum - Program udržitelnosti</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Metalurgija = Metallurgy

ISSN

0543-5846

e-ISSN

—

Svazek periodika

54

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

HR - Chorvatská republika

Počet stran výsledku

4

Strana od-do

187-190

Kód UT WoS článku

000341740000047

EID výsledku v databázi Scopus

—