Effect of CaO/SiO2 ratio on viscosity and structure of slag
Popis výsledku v původním jazyce
The objective of this work is experimental determination of temperature dependences of viscosity of the molten CaO Al2O3 SiO2 system and assessment of impact of CaO/SiO2 ratio on viscosity and structure of this system. Experimental measurements of viscosity were performed with use of the high-temperature viscometer Anton Paar FRS 1 600. Viscosity was measured in a rotational mode during heating at the rate of 3.3 oC/min in the temperature interval from 1 673 to 1 873 K. Viscosity in the molten oxide system is determined by the internal structure. Exact clarification of the change of structure of the oxide system caused by the increased content of CaO was performed by Fourier transform infrared spectroscopy.
Název v anglickém jazyce
Effect of CaO/SiO2 ratio on viscosity and structure of slag
Popis výsledku anglicky
The objective of this work is experimental determination of temperature dependences of viscosity of the molten CaO Al2O3 SiO2 system and assessment of impact of CaO/SiO2 ratio on viscosity and structure of this system. Experimental measurements of viscosity were performed with use of the high-temperature viscometer Anton Paar FRS 1 600. Viscosity was measured in a rotational mode during heating at the rate of 3.3 oC/min in the temperature interval from 1 673 to 1 873 K. Viscosity in the molten oxide system is determined by the internal structure. Exact clarification of the change of structure of the oxide system caused by the increased content of CaO was performed by Fourier transform infrared spectroscopy.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/LO1203" target="_blank" >LO1203: Regionální materiálově technologické výzkumné centrum - Program udržitelnosti</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Metalurgija = Metallurgy
ISSN
0543-5846
e-ISSN
—
Svazek periodika
54
Číslo periodika v rámci svazku
3
Stát vydavatele periodika
HR - Chorvatská republika
Počet stran výsledku
4
Strana od-do
455-458
Kód UT WoS článku
000347363100001
EID výsledku v databázi Scopus
2-s2.0-84925829999