A Kinetics and Morphological Study on the Oxidation Behavior of Ti-4Al-2V Alloy
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F15%3A86095740" target="_blank" >RIV/61989100:27360/15:86095740 - isvavai.cz</a>
Výsledek na webu
<a href="http://link.springer.com/article/10.1007%2Fs11085-015-9539-2" target="_blank" >http://link.springer.com/article/10.1007%2Fs11085-015-9539-2</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1007/s11085-015-9539-2" target="_blank" >10.1007/s11085-015-9539-2</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
A Kinetics and Morphological Study on the Oxidation Behavior of Ti-4Al-2V Alloy
Popis výsledku v původním jazyce
Oxidation behavior of Ti-4Al-2V alloy in air was studied by isothermal thermogravimetry. It was found that the oxidation kinetics are parabolic in the temperature range 450-700 oC. The activation energies for reaction of titanium with oxygen and oxide growth were calculated as 90 and 114 kJ/mol, respectively. Microhardness measurements showed that thermal oxidation at 700 oC could increase the depth of subsurface diffusion zone up to 150 ?m. The morphological studies of oxidized surfaces revealed that the thermal oxidation at 700 oC led to scaling and eventual detachment of the scale from the substrate due to the cracking at the metal/oxide interface.
Název v anglickém jazyce
A Kinetics and Morphological Study on the Oxidation Behavior of Ti-4Al-2V Alloy
Popis výsledku anglicky
Oxidation behavior of Ti-4Al-2V alloy in air was studied by isothermal thermogravimetry. It was found that the oxidation kinetics are parabolic in the temperature range 450-700 oC. The activation energies for reaction of titanium with oxygen and oxide growth were calculated as 90 and 114 kJ/mol, respectively. Microhardness measurements showed that thermal oxidation at 700 oC could increase the depth of subsurface diffusion zone up to 150 ?m. The morphological studies of oxidized surfaces revealed that the thermal oxidation at 700 oC led to scaling and eventual detachment of the scale from the substrate due to the cracking at the metal/oxide interface.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JK - Koroze a povrchové úpravy materiálu
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
N - Vyzkumna aktivita podporovana z neverejnych zdroju
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Oxidation of Metals
ISSN
0030-770X
e-ISSN
—
Svazek periodika
84
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
12
Strana od-do
33-44
Kód UT WoS článku
000357344200003
EID výsledku v databázi Scopus
2-s2.0-84946488320