Structural characteristics of Cr-Mo steels microalloyed with cerium
Popis výsledku v původním jazyce
The results of an experimental study on influence of cerium addition on structural characteristics of 42CrMo4 steel are presented. Alloying with cerium was carried out using profile filled with powdered mixture of mischmetal. The samples were taken fromtwo ingots cast in the VHM's steelworks with standard time of casting of about 14 minutes. Three steel bars from one of the produced ingots were prepared by forging. Chemical composition, macro- and microstructure, X-ray EDX chemical microanalysis, hardness of the all steel samples were obtained. Cerium addition resulted in the formation of micrometer size inclusions which can be utilized for controlling the grain size structure of steel castings. The majority of the particles have settled at the bottompart of the casting, indicating that the convection flow during solidification was very weak. The cerium addition slightly diminished hardness of the steel. A segregation phenomenon causing inhomogeneous distribution of cerium over entir
Název v anglickém jazyce
Structural characteristics of Cr-Mo steels microalloyed with cerium
Popis výsledku anglicky
The results of an experimental study on influence of cerium addition on structural characteristics of 42CrMo4 steel are presented. Alloying with cerium was carried out using profile filled with powdered mixture of mischmetal. The samples were taken fromtwo ingots cast in the VHM's steelworks with standard time of casting of about 14 minutes. Three steel bars from one of the produced ingots were prepared by forging. Chemical composition, macro- and microstructure, X-ray EDX chemical microanalysis, hardness of the all steel samples were obtained. Cerium addition resulted in the formation of micrometer size inclusions which can be utilized for controlling the grain size structure of steel castings. The majority of the particles have settled at the bottompart of the casting, indicating that the convection flow during solidification was very weak. The cerium addition slightly diminished hardness of the steel. A segregation phenomenon causing inhomogeneous distribution of cerium over entir
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Manufacturing Technology
ISSN
1213-2489
e-ISSN
—
Svazek periodika
15
Číslo periodika v rámci svazku
3
Stát vydavatele periodika
CZ - Česká republika
Počet stran výsledku
8
Strana od-do
315-322
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—