Improvements in material characteristics core centrifugally cast rolls

Popis výsledku v původním jazyce

The paper describes the influence of metallurgical processing on the microstructural characteristics of spheroidal graphite cast iron. The iron is used for casting the core of double layer centrifugally cast rolls. Low carbon content in the core spheroidal graphite cast iron supporting metastable solidification was eliminated by managing of metallurgical processing of spheroidal graphite cast iron. The metallurgical quality of the cast iron was controlled by using thermal analysis during all time i.e. melting furnace, through modification and inoculation. The metallurgical quality is documented by metallographic analysis, determination of surface proportion and amount of graphite on surface etched specimen. Test rolls were cast in operating conditions in roll foundry Vítkovické foundries, spol. s r.o. Evaluation of melts and microstructures were made in the laboratories of the VSB-TU Ostrava. (C) 2016. Published by Manufacturing Technology.

Název v anglickém jazyce

Improvements in material characteristics core centrifugally cast rolls

Popis výsledku anglicky

The paper describes the influence of metallurgical processing on the microstructural characteristics of spheroidal graphite cast iron. The iron is used for casting the core of double layer centrifugally cast rolls. Low carbon content in the core spheroidal graphite cast iron supporting metastable solidification was eliminated by managing of metallurgical processing of spheroidal graphite cast iron. The metallurgical quality of the cast iron was controlled by using thermal analysis during all time i.e. melting furnace, through modification and inoculation. The metallurgical quality is documented by metallographic analysis, determination of surface proportion and amount of graphite on surface etched specimen. Test rolls were cast in operating conditions in roll foundry Vítkovické foundries, spol. s r.o. Evaluation of melts and microstructures were made in the laboratories of the VSB-TU Ostrava. (C) 2016. Published by Manufacturing Technology.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/TA04010223" target="_blank" >TA04010223: Výzkum a vývoj výroby odstředivě litých válců s pracovní vrstvou určených pro poslední stolice hotovního pořadí teplé válcovací tratě.</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Manufacturing Technology

ISSN

1213-2489

e-ISSN

—

Svazek periodika

16

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

4

Strana od-do

468-471

Kód UT WoS článku

—

EID výsledku v databázi Scopus

2-s2.0-84964806400