Texture, deformation twinning and hardening in a newly developed Mg-Dy-Al-Zn-Zr alloy processed with high pressure torsion

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F16%3A86099199" target="_blank" >RIV/61989100:27360/16:86099199 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.sciencedirect.com/science/article/pii/S0264127515308042" target="_blank" >http://www.sciencedirect.com/science/article/pii/S0264127515308042</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.matdes.2015.11.062" target="_blank" >10.1016/j.matdes.2015.11.062</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Texture, deformation twinning and hardening in a newly developed Mg-Dy-Al-Zn-Zr alloy processed with high pressure torsion

Popis výsledku v původním jazyce

The influence of severe plastic deformation via high pressure torsion (HPT) on texture, deformation twinning and hardening in a newly developed Mg-Dy-Al-Zn-Zr alloy was observed in this study. Test specimens were cast, solution annealed, aged at 250 oC and 300 oC, and then subject to three revolutions of HPT at room temperature. Microhardness measurementswere performed in order to evaluate structural changes introduced via ageing and deformation processing, while electron backscatter diffraction analyses (EBSD) were performed to evaluate texture and grain misorientations. Results showed that both, ageing temperatures and HPT processing significantly affected texture as well as twinning.Microhardness nearly doubled due to deformation processing, especially for aged samples.

Název v anglickém jazyce

Texture, deformation twinning and hardening in a newly developed Mg-Dy-Al-Zn-Zr alloy processed with high pressure torsion

Popis výsledku anglicky

The influence of severe plastic deformation via high pressure torsion (HPT) on texture, deformation twinning and hardening in a newly developed Mg-Dy-Al-Zn-Zr alloy was observed in this study. Test specimens were cast, solution annealed, aged at 250 oC and 300 oC, and then subject to three revolutions of HPT at room temperature. Microhardness measurementswere performed in order to evaluate structural changes introduced via ageing and deformation processing, while electron backscatter diffraction analyses (EBSD) were performed to evaluate texture and grain misorientations. Results showed that both, ageing temperatures and HPT processing significantly affected texture as well as twinning.Microhardness nearly doubled due to deformation processing, especially for aged samples.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/LO1203" target="_blank" >LO1203: Regionální materiálově technologické výzkumné centrum - Program udržitelnosti</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials and Design

ISSN

0261-3069

e-ISSN

—

Svazek periodika

90

Číslo periodika v rámci svazku

January

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

8

Strana od-do

1090-1099

Kód UT WoS článku

000367235100129

EID výsledku v databázi Scopus

2-s2.0-84952359815