Plastometric study of hot formability of hypereutectoid C-Mn-Cr-V steel

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F16%3A86099335" target="_blank" >RIV/61989100:27360/16:86099335 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Plastometric study of hot formability of hypereutectoid C-Mn-Cr-V steel

Popis výsledku v původním jazyce

Formability of hypereutectoid C-Mn-Cr-V steel in hot condition was investigated with use of plastometric methods. A wide range of deformation temperatures 1 300-640 oC for hot tensile tests was proposed with use of nil-strength temperature (NST), determined by special plastometric method, and as well as with use of the calculated temperatures of phase transformations during heating of the investigated steel. Ultimate tensile strength of the investigated steel was increasing exponentially with the decreasing deformation temperature. Ductility of the investigated steel in hot condition increased with the increasing deformation temperature up to the temperatures ranging from 1 150 to 1 250 oC, after which a sharp decline of formability took place in investigated material. (C) 2016, Faculty of Metallurgy. All rights reserved.

Název v anglickém jazyce

Plastometric study of hot formability of hypereutectoid C-Mn-Cr-V steel

Popis výsledku anglicky

Formability of hypereutectoid C-Mn-Cr-V steel in hot condition was investigated with use of plastometric methods. A wide range of deformation temperatures 1 300-640 oC for hot tensile tests was proposed with use of nil-strength temperature (NST), determined by special plastometric method, and as well as with use of the calculated temperatures of phase transformations during heating of the investigated steel. Ultimate tensile strength of the investigated steel was increasing exponentially with the decreasing deformation temperature. Ductility of the investigated steel in hot condition increased with the increasing deformation temperature up to the temperatures ranging from 1 150 to 1 250 oC, after which a sharp decline of formability took place in investigated material. (C) 2016, Faculty of Metallurgy. All rights reserved.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/LO1203" target="_blank" >LO1203: Regionální materiálově technologické výzkumné centrum - Program udržitelnosti</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Metalurgija

ISSN

0543-5846

e-ISSN

—

Svazek periodika

55

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

HR - Chorvatská republika

Počet stran výsledku

4

Strana od-do

365-368

Kód UT WoS článku

000372344500019

EID výsledku v databázi Scopus

—