Influence of Casting Speed on Solidification of Continuously Cast Round Steel Billets
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F17%3A10235762" target="_blank" >RIV/61989100:27360/17:10235762 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Influence of Casting Speed on Solidification of Continuously Cast Round Steel Billets
Popis výsledku v původním jazyce
The aim of this paper is the study of solidification of continuously cast round steel billets, with focus on the centerline porosity formation. This work represents the basic procedure of experimental study using numerical modelling in commercial simulation software ProCAST, which was used to verify the technology of continuous casting of round steel billets. The attention was paid especially to prediction of solidification of continuously cast steel billets and centerline porosity formation related to casting speed. The centerline porosity formation is closely related to the solidification process, especially to the angle formed between the opposite solidification fronts. The angle formed between the solidification fronts increases with shortening of metallurgical length due to reduction of the casting speed. Reduction of the casting speed has therefore possible influence on minimization of the centerline porosity.
Název v anglickém jazyce
Influence of Casting Speed on Solidification of Continuously Cast Round Steel Billets
Popis výsledku anglicky
The aim of this paper is the study of solidification of continuously cast round steel billets, with focus on the centerline porosity formation. This work represents the basic procedure of experimental study using numerical modelling in commercial simulation software ProCAST, which was used to verify the technology of continuous casting of round steel billets. The attention was paid especially to prediction of solidification of continuously cast steel billets and centerline porosity formation related to casting speed. The centerline porosity formation is closely related to the solidification process, especially to the angle formed between the opposite solidification fronts. The angle formed between the solidification fronts increases with shortening of metallurgical length due to reduction of the casting speed. Reduction of the casting speed has therefore possible influence on minimization of the centerline porosity.
Klasifikace
Druh
J<sub>ost</sub> - Ostatní články v recenzovaných periodicích
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/LO1203" target="_blank" >LO1203: Regionální materiálově technologické výzkumné centrum - Program udržitelnosti</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2017
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Hutnické listy
ISSN
0018-8069
e-ISSN
—
Svazek periodika
60
Číslo periodika v rámci svazku
2
Stát vydavatele periodika
CZ - Česká republika
Počet stran výsledku
6
Strana od-do
22-27
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—