Potentiodynamic polarization and electrochemical impedance spectroscopy used for prediction of nitinol stent's lifetime

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F17%3A10238034" target="_blank" >RIV/61989100:27360/17:10238034 - isvavai.cz</a>

Výsledek na webu

<a href="https://www.scientific.net/KEM.741.50" target="_blank" >https://www.scientific.net/KEM.741.50</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.741.50" target="_blank" >10.4028/www.scientific.net/KEM.741.50</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Potentiodynamic polarization and electrochemical impedance spectroscopy used for prediction of nitinol stent's lifetime

Popis výsledku v původním jazyce

This paper is focused on prediction of nitinol stents lifetime. Stents have been tested before and after mechanical loading. Corrosion tests of mechanically loaded specimens indicated impairment of corrosion resistance and SEM observation confirmed presence of micro cracks in surface oxide layer created during heat treatment. Electrochemical impedance spectroscopy and potentiodynamic polarization measurements in physiological solution (0.9% NaCl in H2O) was used for these particular experiments. Corrosion rate and other parameters have been used for calculation of released nickel ions weight and prediction of application lifetime. © 2017 Trans Tech Publications, Switzerland.

Název v anglickém jazyce

Potentiodynamic polarization and electrochemical impedance spectroscopy used for prediction of nitinol stent's lifetime

Popis výsledku anglicky

This paper is focused on prediction of nitinol stents lifetime. Stents have been tested before and after mechanical loading. Corrosion tests of mechanically loaded specimens indicated impairment of corrosion resistance and SEM observation confirmed presence of micro cracks in surface oxide layer created during heat treatment. Electrochemical impedance spectroscopy and potentiodynamic polarization measurements in physiological solution (0.9% NaCl in H2O) was used for these particular experiments. Corrosion rate and other parameters have been used for calculation of released nickel ions weight and prediction of application lifetime. © 2017 Trans Tech Publications, Switzerland.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Key Engineering Materials. Volume 741

ISBN

978-3-0357-1127-1

ISSN

1013-9826

e-ISSN

1662-9795

Počet stran výsledku

7

Strana od-do

50-56

Název nakladatele

Trans Tech Publications

Místo vydání

Uetikon-Zuerich

Místo konání akce

Yokohama

Datum konání akce

1. 11. 2016

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—