Microstructural stability of fully lamellar Ti-45Al-5Nb-0.2B-0.75C alloy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F17%3A10238124" target="_blank" >RIV/61989100:27360/17:10238124 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Microstructural stability of fully lamellar Ti-45Al-5Nb-0.2B-0.75C alloy

Popis výsledku v původním jazyce

The microstructural stability of fully lamellar γ-TiAl alloy was studied under thermal exposure at 750, 850 and 950 °C for 3400 h. The microstructure analysis show that the most dominant change in the microstructure was that the α2 lamellae thinned gradually and thinning was more pronounced with increasing temperature and with increasing time. Formation of recrystallized γ grains and Ti2AlC carbides were also observed especially during the temperature 850 and 950 °C after prolonged heat treatment. The effect of microstructural changes during the thermal exposure on mechanical properties was evaluated and discussed.

Název v anglickém jazyce

Microstructural stability of fully lamellar Ti-45Al-5Nb-0.2B-0.75C alloy

Popis výsledku anglicky

The microstructural stability of fully lamellar γ-TiAl alloy was studied under thermal exposure at 750, 850 and 950 °C for 3400 h. The microstructure analysis show that the most dominant change in the microstructure was that the α2 lamellae thinned gradually and thinning was more pronounced with increasing temperature and with increasing time. Formation of recrystallized γ grains and Ti2AlC carbides were also observed especially during the temperature 850 and 950 °C after prolonged heat treatment. The effect of microstructural changes during the thermal exposure on mechanical properties was evaluated and discussed.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

<a href="/cs/project/LO1203" target="_blank" >LO1203: Regionální materiálově technologické výzkumné centrum - Program udržitelnosti</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

METAL 2017: conference proceedings : 26th International Conference on Metallurgy and Materials : (reviewed version) : May 24th-26th 2017, Hotel Voroněž I, Brno, Czech Republic, EU

ISBN

978-80-87294-79-6

ISSN

—

e-ISSN

neuvedeno

Počet stran výsledku

6

Strana od-do

1676-1681

Název nakladatele

Tanger

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

24. 5. 2017

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—