EFFECT OF LONG-TERM AGEING AT 475 oC ON PROPERTIES AND MICROSTRUCTURE OF CUSTOM 465 STEEL

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F17%3A10238291" target="_blank" >RIV/61989100:27360/17:10238291 - isvavai.cz</a>

Výsledek na webu

<a href="https://www.metalconference.eu/files/uploads/02/METAL2017_conference_proceedings_content.pdf" target="_blank" >https://www.metalconference.eu/files/uploads/02/METAL2017_conference_proceedings_content.pdf</a>

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

EFFECT OF LONG-TERM AGEING AT 475 oC ON PROPERTIES AND MICROSTRUCTURE OF CUSTOM 465 STEEL

Popis výsledku v původním jazyce

The steels with high chromium content are known to suffer embrittlement at elevated temperature induced either by decomposition of the microstructure into two arranged solid solutions α+α&apos; (embrittlement at 475 oC) or by precipitation of chromium-rich brittle phase. Martensitic precipitation hardening steels belong among materials having chromium content close to the minimum embrittlement concentration and in some circumstances there could be possibility of prolonged exposure of these steels at elevated temperatures. The effect of long-term ageing (1,000, 2,000 and 3,000 hours at 475 oC) on the material properties, microstructure and substructure of precipitation hardening martensitic stainless steel CUSTOM 465 was analysed and the additional precipitation of very fine particles of intermetallic phases and also decomposition of solid solution α into chromium-rich particles of the phase α&apos; with nanometric size was found. Despite expectations a slight decrease of strength and impact energy was detected after ageing at 475 oC as a result of stabilization of reverted austenite, which completely compensated the effect of the additional precipitation hardening of martensite. The total content of reverted austenite even doubled after ageing in comparison with the as-received state, although the ageing temperature was significantly lower than the temperature Ac1 of the steel.

Název v anglickém jazyce

EFFECT OF LONG-TERM AGEING AT 475 oC ON PROPERTIES AND MICROSTRUCTURE OF CUSTOM 465 STEEL

Popis výsledku anglicky

The steels with high chromium content are known to suffer embrittlement at elevated temperature induced either by decomposition of the microstructure into two arranged solid solutions α+α&apos; (embrittlement at 475 oC) or by precipitation of chromium-rich brittle phase. Martensitic precipitation hardening steels belong among materials having chromium content close to the minimum embrittlement concentration and in some circumstances there could be possibility of prolonged exposure of these steels at elevated temperatures. The effect of long-term ageing (1,000, 2,000 and 3,000 hours at 475 oC) on the material properties, microstructure and substructure of precipitation hardening martensitic stainless steel CUSTOM 465 was analysed and the additional precipitation of very fine particles of intermetallic phases and also decomposition of solid solution α into chromium-rich particles of the phase α&apos; with nanometric size was found. Despite expectations a slight decrease of strength and impact energy was detected after ageing at 475 oC as a result of stabilization of reverted austenite, which completely compensated the effect of the additional precipitation hardening of martensite. The total content of reverted austenite even doubled after ageing in comparison with the as-received state, although the ageing temperature was significantly lower than the temperature Ac1 of the steel.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

<a href="/cs/project/LO1203" target="_blank" >LO1203: Regionální materiálově technologické výzkumné centrum - Program udržitelnosti</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

METAL 2017: conference proceedings : 26th International Conference on Metallurgy and Materials : (reviewed version) : May 24th-26th 2017, Hotel Voroněž I, Brno, Czech Republic, EU

ISBN

978-80-87294-79-6

ISSN

—

e-ISSN

neuvedeno

Počet stran výsledku

6

Strana od-do

991- 996

Název nakladatele

Tanger

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

24. 5. 2017

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000434346900158