Influencing of transformation kinetic of 25CrMo4 steel by the thermomechanical parameters
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F18%3A10240973" target="_blank" >RIV/61989100:27360/18:10240973 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Influencing of transformation kinetic of 25CrMo4 steel by the thermomechanical parameters
Popis výsledku v původním jazyce
The aim of the contribution is creation of transformation diagrams of hypoeutectoid 25CrMo4 steel that is used for tube production for the OCTG (Oil Country Tubular Goods) industry. For a comparison purpose, the CCT diagrams with and even without influence of previous deformation were assembled. In addition, the DCCT diagram (i.e. with previous deformation influence) was exposed to different austenitization conditions. The transformation diagrams were assembled on the basis of dilatometric tests which were confronted with the metallographic analysis and hardness measurement. Due to the influence of previous deformation and different austenitization conditions, peremptory movements of curves in the assembled transformation diagrams were occurred, which, of course, was reflected also on the structure and hardness, respectively. After the previous deformation, the structures of samples had considerably increased share of quenching phases, including of share of acicular ferrite. This, of course, was manifested by increased values of hardness.
Název v anglickém jazyce
Influencing of transformation kinetic of 25CrMo4 steel by the thermomechanical parameters
Popis výsledku anglicky
The aim of the contribution is creation of transformation diagrams of hypoeutectoid 25CrMo4 steel that is used for tube production for the OCTG (Oil Country Tubular Goods) industry. For a comparison purpose, the CCT diagrams with and even without influence of previous deformation were assembled. In addition, the DCCT diagram (i.e. with previous deformation influence) was exposed to different austenitization conditions. The transformation diagrams were assembled on the basis of dilatometric tests which were confronted with the metallographic analysis and hardness measurement. Due to the influence of previous deformation and different austenitization conditions, peremptory movements of curves in the assembled transformation diagrams were occurred, which, of course, was reflected also on the structure and hardness, respectively. After the previous deformation, the structures of samples had considerably increased share of quenching phases, including of share of acicular ferrite. This, of course, was manifested by increased values of hardness.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/FV10253" target="_blank" >FV10253: Výzkum a vývoj progresivních mikrolegovaných materiálů pro teplotně řízené válcování a ochlazování s následným zušlechtěním bezešvých trub pro použití v oblasti OCTG a strojním průmyslu</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2018
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
METAL 2018 : conference proceedings : reviewed version : 27th International Conference on Metallurgy and Materials : May 23rd-25th 2018, Hotel Voronez I, Brno, Czech Republic, EU
ISBN
978-80-87294-84-0
ISSN
—
e-ISSN
neuvedeno
Počet stran výsledku
6
Strana od-do
236-241
Název nakladatele
Tanger
Místo vydání
Ostrava
Místo konání akce
Brno
Datum konání akce
23. 5. 2018
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—