Selected properties of high strength manganese steels
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F18%3A10241501" target="_blank" >RIV/61989100:27360/18:10241501 - isvavai.cz</a>
Výsledek na webu
<a href="https://www.metalconference.eu/files/uploads/02/Sbornik_Metal_2018_Content.pdf" target="_blank" >https://www.metalconference.eu/files/uploads/02/Sbornik_Metal_2018_Content.pdf</a>
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Selected properties of high strength manganese steels
Popis výsledku v původním jazyce
Work is aimed at three laboratory manufactured high strength manganese steels after cast, rolling and aging process (at 500 oC after 6, 12, 30 and/or 60 minutes of dwell). Micro-hardnesses (HV0.2) as well as potential k-carbides formation of micro- and/or nano-size and microstructures characters of all treatment modes are mutually compared. Revealed disproportions are explained by differences in chemical composition and in finishing hot rolling temperature leading to undesirable coarser k-carbides formation on the austenite-austenite, resp. austenite-ferite interphase. Simultaneously, changes in selected thermos-physical parameters both after hot rolling and after subsequent aging (560 oC / 6 minutes) were studied. between micro-hardness and those thermos-physical parameters some proportionality was observed.
Název v anglickém jazyce
Selected properties of high strength manganese steels
Popis výsledku anglicky
Work is aimed at three laboratory manufactured high strength manganese steels after cast, rolling and aging process (at 500 oC after 6, 12, 30 and/or 60 minutes of dwell). Micro-hardnesses (HV0.2) as well as potential k-carbides formation of micro- and/or nano-size and microstructures characters of all treatment modes are mutually compared. Revealed disproportions are explained by differences in chemical composition and in finishing hot rolling temperature leading to undesirable coarser k-carbides formation on the austenite-austenite, resp. austenite-ferite interphase. Simultaneously, changes in selected thermos-physical parameters both after hot rolling and after subsequent aging (560 oC / 6 minutes) were studied. between micro-hardness and those thermos-physical parameters some proportionality was observed.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/LO1203" target="_blank" >LO1203: Regionální materiálově technologické výzkumné centrum - Program udržitelnosti</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2018
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
METAL 2018 : conference proceedings : reviewed version : 27th International Conference on Metallurgy and Materials : May 23rd-25th 2018, Hotel Voronez I, Brno, Czech Republic, EU
ISBN
978-80-87294-84-0
ISSN
—
e-ISSN
neuvedeno
Počet stran výsledku
6
Strana od-do
789-794
Název nakladatele
Tanger
Místo vydání
Ostrava
Místo konání akce
Brno
Datum konání akce
23. 5. 2018
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—