Synthesis and characterization of erbium oxide nanocrystallites
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F19%3A10236617" target="_blank" >RIV/61989100:27360/19:10236617 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/61989100:27640/19:10236617
Výsledek na webu
<a href="https://www.ingentaconnect.com/content/asp/jnn/2019/00000019/00000005/art00064%3bjsessionid=3tk5g3qq7ctv.x-ic-live-03" target="_blank" >https://www.ingentaconnect.com/content/asp/jnn/2019/00000019/00000005/art00064%3bjsessionid=3tk5g3qq7ctv.x-ic-live-03</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1166/jnn.2019.15857" target="_blank" >10.1166/jnn.2019.15857</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Synthesis and characterization of erbium oxide nanocrystallites
Popis výsledku v původním jazyce
The present article describes a method of the preparation of erbium oxide nanocrystallites (nano Er2O3) via thermal decomposition of a transient complex formed in situ from Er(NO3)3·5H2O and glycine. Decomposition of the complex occurred at about of (250 +- 10) oC. Ultra-fine light pink powder of erbium oxide nanocrystallites was obtained via this method. The resulting nanocrystallites were characterized using X-ray powder diffraction analysis, which showed the nanocrystallites having the crystallite size equal to 10 nm. Morphology of the nanocrystallites was examined by scanning and transmission electron microscopy. Electron diffraction observed in transmission electron microscopy corresponds to the results obtained from X-ray diffraction analysis. The elemental composition of the product was confirmed EDS analysis.
Název v anglickém jazyce
Synthesis and characterization of erbium oxide nanocrystallites
Popis výsledku anglicky
The present article describes a method of the preparation of erbium oxide nanocrystallites (nano Er2O3) via thermal decomposition of a transient complex formed in situ from Er(NO3)3·5H2O and glycine. Decomposition of the complex occurred at about of (250 +- 10) oC. Ultra-fine light pink powder of erbium oxide nanocrystallites was obtained via this method. The resulting nanocrystallites were characterized using X-ray powder diffraction analysis, which showed the nanocrystallites having the crystallite size equal to 10 nm. Morphology of the nanocrystallites was examined by scanning and transmission electron microscopy. Electron diffraction observed in transmission electron microscopy corresponds to the results obtained from X-ray diffraction analysis. The elemental composition of the product was confirmed EDS analysis.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
21001 - Nano-materials (production and properties)
Návaznosti výsledku
Projekt
<a href="/cs/project/LO1203" target="_blank" >LO1203: Regionální materiálově technologické výzkumné centrum - Program udržitelnosti</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2019
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of nanoscience and nanotechnology
ISSN
1533-4880
e-ISSN
—
Svazek periodika
19
Číslo periodika v rámci svazku
5
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
4
Strana od-do
"2934–2937"
Kód UT WoS článku
000458402700064
EID výsledku v databázi Scopus
—