High-temperature deformation properties of CuCr0.6 alloy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F19%3A10243032" target="_blank" >RIV/61989100:27360/19:10243032 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.elis.sk/download_file.php?product_id=6420&session_id=6l7gqmb9qelsn3hv5svn4cb1q3" target="_blank" >http://www.elis.sk/download_file.php?product_id=6420&session_id=6l7gqmb9qelsn3hv5svn4cb1q3</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.4149/km_2019_6_407" target="_blank" >10.4149/km_2019_6_407</a>

Jazyk výsledku

angličtina

Název v původním jazyce

High-temperature deformation properties of CuCr0.6 alloy

Popis výsledku v původním jazyce

The submitted paper aimed to investigate the hot deformation behavior of CuCr0.6 alloy. Nil strength temperature of 1349 K and nil ductility temperature of 1313 K have been experimentally determined. Formability is monotonously increased with the decrease of forming temperature in the temperature range from 923 K to approx. 1273 K. The flow stress curves were obtained in the forming temperature interval of 923-1223 K and at a strain rate of 0.1-10 s(-1). After their analysis, the hot deformation activation energy of 340 kJ mol(-1) was calculated for peak stress and 393 kJ mol(-1) for steady state. This proves that the value of the activation energy depends upon a strain size.

Název v anglickém jazyce

High-temperature deformation properties of CuCr0.6 alloy

Popis výsledku anglicky

The submitted paper aimed to investigate the hot deformation behavior of CuCr0.6 alloy. Nil strength temperature of 1349 K and nil ductility temperature of 1313 K have been experimentally determined. Formability is monotonously increased with the decrease of forming temperature in the temperature range from 923 K to approx. 1273 K. The flow stress curves were obtained in the forming temperature interval of 923-1223 K and at a strain rate of 0.1-10 s(-1). After their analysis, the hot deformation activation energy of 340 kJ mol(-1) was calculated for peak stress and 393 kJ mol(-1) for steady state. This proves that the value of the activation energy depends upon a strain size.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

<a href="/cs/project/EF17_049%2F0008399" target="_blank" >EF17_049/0008399: Rozvoj mezisektorové spolupráce RMTVC s aplikační sférou v oblasti výzkumu progresivních a inovací klasických kovových materiálů a technologií s využitím metod modelování</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2019

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Kovové materiály

ISSN

0023-432X

e-ISSN

—

Svazek periodika

57

Číslo periodika v rámci svazku

6

Stát vydavatele periodika

SK - Slovenská republika

Počet stran výsledku

8

Strana od-do

407-414

Kód UT WoS článku

000497701100005

EID výsledku v databázi Scopus

—