Simulation of magnetization reversal and hysteretic loops of (Nd,Pr)2Fe14B magnets at low temperatures

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F19%3A10244338" target="_blank" >RIV/61989100:27360/19:10244338 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Simulation of magnetization reversal and hysteretic loops of (Nd,Pr)2Fe14B magnets at low temperatures

Popis výsledku v původním jazyce

In the present work, the computer simulation of hysteresis loops of (Nd1-xPrx)2Fe14B compounds with different Pr contents was performed for a temperature range of 300-5 K. The simulation results suggest that the alloying of Nd2Fe14B with Pr (1) leads to reducing the negative effect of the spin-reorientation phase transition on the residual magnetization of the compound (Nd1-xPrx)2Fe14B, (2) reduces the slope of the demagnetization curve making the hysteresis loop more rectangular, (3) does not have a noticeable effect on the maximum value of the coercive force, shifting its maximum to lower temperatures as the Pr content increases. Thus, the alloying of Nd2Fe14B-based compositions with Pr can increase the temperature stability of the hysteresis characteristics of permanent magnets and ensures their operation at low temperatures without loss of magnetic properties. (C) 2019 TANGER Ltd., Ostrava.

Název v anglickém jazyce

Simulation of magnetization reversal and hysteretic loops of (Nd,Pr)2Fe14B magnets at low temperatures

Popis výsledku anglicky

In the present work, the computer simulation of hysteresis loops of (Nd1-xPrx)2Fe14B compounds with different Pr contents was performed for a temperature range of 300-5 K. The simulation results suggest that the alloying of Nd2Fe14B with Pr (1) leads to reducing the negative effect of the spin-reorientation phase transition on the residual magnetization of the compound (Nd1-xPrx)2Fe14B, (2) reduces the slope of the demagnetization curve making the hysteresis loop more rectangular, (3) does not have a noticeable effect on the maximum value of the coercive force, shifting its maximum to lower temperatures as the Pr content increases. Thus, the alloying of Nd2Fe14B-based compositions with Pr can increase the temperature stability of the hysteresis characteristics of permanent magnets and ensures their operation at low temperatures without loss of magnetic properties. (C) 2019 TANGER Ltd., Ostrava.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20500 - Materials engineering

Projekt

<a href="/cs/project/LTARF18031" target="_blank" >LTARF18031: Vývoj fyzikálně-chemických a inženýrských základů pro iniciaci inovativní úsporné technologie výroby vysoce výkonných permanentních magnetů na bázi (Nd,R)-Fe-B (R = Pr, Tb, Dy, Ho) s nízkým obsahem kovů vzácných zemin</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2019

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

METAL 2019 : conference proceedings : peer reviewed : 28th International Conference on Metallurgy and Materials : May 22nd-24th 2019, Hotel Voronez I, Brno, Czech Republic, EU

ISBN

978-80-87294-92-5

ISSN

—

e-ISSN

—

Počet stran výsledku

7

Strana od-do

1621-1627

Název nakladatele

Tanger

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

22. 5. 2019

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—