Alkali-Activated Metakaolin and Fly Ash as Unfired Ceramic Bonding Systems

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F21%3A10247546" target="_blank" >RIV/61989100:27360/21:10247546 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61989100:27710/21:10247546

Výsledek na webu

<a href="https://www.mdpi.com/2075-163X/11/2/197/htm" target="_blank" >https://www.mdpi.com/2075-163X/11/2/197/htm</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.3390/min11020197" target="_blank" >10.3390/min11020197</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Alkali-Activated Metakaolin and Fly Ash as Unfired Ceramic Bonding Systems

Popis výsledku v původním jazyce

Metakaolin (MK) prepared by the calcination of kaolin at 550 degrees C and fly ash (FA) from the combustion of black coal in a granulating boiler were used to prepare unfired ceramic bonding systems via the alkali activation process. A long-term stability of the mechanical properties of the prepared samples similar to the unfired ceramic systems was observed. The optimal metakaolin and fly ash ratio, the type of the activator (NaOH or water glass) and its concentration were evaluated after the hydration in: a) laboratory conditions; b) hydration box; and c) under the hydrothermal activation. Raw materials and the samples prepared by alkali activation process were characterized by XRD, XRF, TG/DTA, and FTIR methods. The mechanical properties of the prepared samples were tested using a compressive strength test after 2, 28 and 56 days of hydration. The compressive strengths of 16 and 24 MPa after 28 days of hydration were reached for FA samples activated with water glass. The alkali activation of MK was successful in the NaOH solution of the molar concentration above 5 M. The compressive strength values of metakaolin, activated hydrothermally and hydrated at laboratory conditions, reached 11.2 and 5.5 MPa, respectively, for 5 M activator of NaOH.

Název v anglickém jazyce

Alkali-Activated Metakaolin and Fly Ash as Unfired Ceramic Bonding Systems

Popis výsledku anglicky

Metakaolin (MK) prepared by the calcination of kaolin at 550 degrees C and fly ash (FA) from the combustion of black coal in a granulating boiler were used to prepare unfired ceramic bonding systems via the alkali activation process. A long-term stability of the mechanical properties of the prepared samples similar to the unfired ceramic systems was observed. The optimal metakaolin and fly ash ratio, the type of the activator (NaOH or water glass) and its concentration were evaluated after the hydration in: a) laboratory conditions; b) hydration box; and c) under the hydrothermal activation. Raw materials and the samples prepared by alkali activation process were characterized by XRD, XRF, TG/DTA, and FTIR methods. The mechanical properties of the prepared samples were tested using a compressive strength test after 2, 28 and 56 days of hydration. The compressive strengths of 16 and 24 MPa after 28 days of hydration were reached for FA samples activated with water glass. The alkali activation of MK was successful in the NaOH solution of the molar concentration above 5 M. The compressive strength values of metakaolin, activated hydrothermally and hydrated at laboratory conditions, reached 11.2 and 5.5 MPa, respectively, for 5 M activator of NaOH.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20500 - Materials engineering

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2021

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Minerals

ISSN

2075-163X

e-ISSN

—

Svazek periodika

11

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

16

Strana od-do

—

Kód UT WoS článku

000622846600001

EID výsledku v databázi Scopus

—