Rheological Characteristics of Fe-C-Cr(Ni) Alloys
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F23%3A10252941" target="_blank" >RIV/61989100:27360/23:10252941 - isvavai.cz</a>
Výsledek na webu
<a href="https://www.mdpi.com/1996-1944/16/7/2656" target="_blank" >https://www.mdpi.com/1996-1944/16/7/2656</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.3390/ma16072656" target="_blank" >10.3390/ma16072656</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Rheological Characteristics of Fe-C-Cr(Ni) Alloys
Popis výsledku v původním jazyce
The principal objective of this project was to investigate the rheological properties of Fe-C- Cr and Fe-C-Ni-based low-alloy steels using an Anton Paar high-temperature rotational viscometer up to 1550 C-?. The emphasis was placed on determining the liquidus temperatures and evaluating the flow and viscosity curves and the temperature dependence of dynamic viscosity. All were studied depending on the change in the content of chromium (0.010-4.863 wt%), nickel (0.001-4.495 wt%), and carbon (0.043-1.563 wt%). It was shown that the dynamic viscosity decreases with increasing nickel content and increases with increasing carbon and chromium content. The experimental data of the flow curves were fitted using the Herschel-Bulkley model with a good agreement between the measured and calculated values. Characterization of the internal structure was performed by SEM and EDX analyses, confirming non-significant changes in the microstructure of the original and remelted samples. The phase composition of the selected samples was also determined using JMatPro 12.0 simulation software (Sente Software Ltd., Guildford, UK).
Název v anglickém jazyce
Rheological Characteristics of Fe-C-Cr(Ni) Alloys
Popis výsledku anglicky
The principal objective of this project was to investigate the rheological properties of Fe-C- Cr and Fe-C-Ni-based low-alloy steels using an Anton Paar high-temperature rotational viscometer up to 1550 C-?. The emphasis was placed on determining the liquidus temperatures and evaluating the flow and viscosity curves and the temperature dependence of dynamic viscosity. All were studied depending on the change in the content of chromium (0.010-4.863 wt%), nickel (0.001-4.495 wt%), and carbon (0.043-1.563 wt%). It was shown that the dynamic viscosity decreases with increasing nickel content and increases with increasing carbon and chromium content. The experimental data of the flow curves were fitted using the Herschel-Bulkley model with a good agreement between the measured and calculated values. Characterization of the internal structure was performed by SEM and EDX analyses, confirming non-significant changes in the microstructure of the original and remelted samples. The phase composition of the selected samples was also determined using JMatPro 12.0 simulation software (Sente Software Ltd., Guildford, UK).
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/EF17_049%2F0008399" target="_blank" >EF17_049/0008399: Rozvoj mezisektorové spolupráce RMTVC s aplikační sférou v oblasti výzkumu progresivních a inovací klasických kovových materiálů a technologií s využitím metod modelování</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2023
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Materials
ISSN
1996-1944
e-ISSN
1996-1944
Svazek periodika
16
Číslo periodika v rámci svazku
7
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
13
Strana od-do
—
Kód UT WoS článku
000969632100001
EID výsledku v databázi Scopus
2-s2.0-85152671260