SIMULATION OF HOT CONTINUOUS ROLLING OF A PLAIN CARBON STEEL USING THE MAXSTRAIN II(R) MULTI-AXIS DEFORMATION SYSTEM
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F23%3A10253907" target="_blank" >RIV/61989100:27360/23:10253907 - isvavai.cz</a>
Výsledek na webu
<a href="https://journals.pan.pl/dlibra/publication/142456/edition/127413/content" target="_blank" >https://journals.pan.pl/dlibra/publication/142456/edition/127413/content</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.24425/amm.2023.142456" target="_blank" >10.24425/amm.2023.142456</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
SIMULATION OF HOT CONTINUOUS ROLLING OF A PLAIN CARBON STEEL USING THE MAXSTRAIN II(R) MULTI-AXIS DEFORMATION SYSTEM
Popis výsledku v původním jazyce
A simple methodology was used for calculating the equivalent strain values during forming the sample alternately in two mutually perpendicular directions. This method reflects an unexpected material flow out of the nominal deformation zone when forming on the MAXStrain II device. Thus it was possible to perform two temperature variants of the simulation of continuous rolling and cooling of a long product made of steel containing 0.17% C and 0.80% Mn. Increasing the finishing temperature from 900 degrees C to 950 degrees C and decreasing the cooling rate from 10 degrees C/s to 5 degrees C/s led to a decrease in the content of acicular ferrite and bainite and an increase in the mean grain size of proeutectoid ferrite from about 8 gm to 14 gm. The result was a change in the hardness of the material by 15%.
Název v anglickém jazyce
SIMULATION OF HOT CONTINUOUS ROLLING OF A PLAIN CARBON STEEL USING THE MAXSTRAIN II(R) MULTI-AXIS DEFORMATION SYSTEM
Popis výsledku anglicky
A simple methodology was used for calculating the equivalent strain values during forming the sample alternately in two mutually perpendicular directions. This method reflects an unexpected material flow out of the nominal deformation zone when forming on the MAXStrain II device. Thus it was possible to perform two temperature variants of the simulation of continuous rolling and cooling of a long product made of steel containing 0.17% C and 0.80% Mn. Increasing the finishing temperature from 900 degrees C to 950 degrees C and decreasing the cooling rate from 10 degrees C/s to 5 degrees C/s led to a decrease in the content of acicular ferrite and bainite and an increase in the mean grain size of proeutectoid ferrite from about 8 gm to 14 gm. The result was a change in the hardness of the material by 15%.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20500 - Materials engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/EF17_049%2F0008399" target="_blank" >EF17_049/0008399: Rozvoj mezisektorové spolupráce RMTVC s aplikační sférou v oblasti výzkumu progresivních a inovací klasických kovových materiálů a technologií s využitím metod modelování</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2023
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Archives of Metallurgy and Materials
ISSN
1733-3490
e-ISSN
2300-1909
Svazek periodika
68
Číslo periodika v rámci svazku
2
Stát vydavatele periodika
PL - Polská republika
Počet stran výsledku
7
Strana od-do
741-747
Kód UT WoS článku
001101214400040
EID výsledku v databázi Scopus
—