Preparation of Mg-vermiculite nanoparticles using potassium persulfate
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27640%2F06%3A00014372" target="_blank" >RIV/61989100:27640/06:00014372 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Preparation of Mg-vermiculite nanoparticles using potassium persulfate
Popis výsledku v původním jazyce
Delamination/exfoliation process of the Mg-vermiculite (Letovice, CZE), particles with size less than 5 μm, was studied after potassium persulfate treatment and compared with known method of hydrogen peroxide treatment. X-ray powder diffraction patterns showed that treatment of Mg-vermiculite with different molar concentration of persulfate at the temperature 60 °C for 2 h. caused reduction of relative intensity of the basal 001 diffraction to the 15 %, 9 % and 4 %, respectively, compared to intensity of 001 diffraction of untreated Mg-vermiculite (100 %). On the other hand Irel. of the 001 diffraction of Mg-vermiculite after treatment with 30 % and 50 % hydrogen peroxide decreased only to Irel. = 36 % and 32 %, respectively. Atomic Force Microscopy and Scanning Electron Microscopy verified effect of the treatment on structure degradation connected with higher degree of delamination/exfoliation of the particles and their cracking into nano-sized particles.
Název v anglickém jazyce
Preparation of Mg-vermiculite nanoparticles using potassium persulfate
Popis výsledku anglicky
Delamination/exfoliation process of the Mg-vermiculite (Letovice, CZE), particles with size less than 5 μm, was studied after potassium persulfate treatment and compared with known method of hydrogen peroxide treatment. X-ray powder diffraction patterns showed that treatment of Mg-vermiculite with different molar concentration of persulfate at the temperature 60 °C for 2 h. caused reduction of relative intensity of the basal 001 diffraction to the 15 %, 9 % and 4 %, respectively, compared to intensity of 001 diffraction of untreated Mg-vermiculite (100 %). On the other hand Irel. of the 001 diffraction of Mg-vermiculite after treatment with 30 % and 50 % hydrogen peroxide decreased only to Irel. = 36 % and 32 %, respectively. Atomic Force Microscopy and Scanning Electron Microscopy verified effect of the treatment on structure degradation connected with higher degree of delamination/exfoliation of the particles and their cracking into nano-sized particles.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JJ - Ostatní materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA205%2F05%2F2548" target="_blank" >GA205/05/2548: Nanomateriály založené na strukturně modifikovaných jílových minerálech</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2006
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Nanoscience and Nanotechnology
ISSN
1533-4880
e-ISSN
—
Svazek periodika
6
Číslo periodika v rámci svazku
8
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
4
Strana od-do
2484-2488
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—