Katalytická depozice vláknitých uhlíkatých materiálů na korundu

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27640%2F07%3A00015369" target="_blank" >RIV/61989100:27640/07:00015369 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Filamentous Carbon Catalytic Deposition of coal-tar pitch fraction on corundum

Popis výsledku v původním jazyce

Our work was focused on deposition of volatile hydrocarbons of carbonaceous precursor on corundum wafer, taking advantage of a metallic catalyst incorporated in precursor. Coal tar-pitch, namely a fraction soluble in toluene, served as precursor materialfor deposition of filamentous material. The toluenesoluble fraction of tar-pitch originally contained metallic particles of iron and nickel. During heat treatment up to 10008C, metallic particles accompanied the volatile hydrocarbons conducive to forming a filamentous deposit. The deposit obtained demonstrates a semicrystalline material that has an irregular filamentous structure with an average filament diameter of 30 mm. The presence of catalysts after the deposition process was proved in the depositbut catalysts were not found in the residuum.

Název v anglickém jazyce

Filamentous Carbon Catalytic Deposition of coal-tar pitch fraction on corundum

Popis výsledku anglicky

Our work was focused on deposition of volatile hydrocarbons of carbonaceous precursor on corundum wafer, taking advantage of a metallic catalyst incorporated in precursor. Coal tar-pitch, namely a fraction soluble in toluene, served as precursor materialfor deposition of filamentous material. The toluenesoluble fraction of tar-pitch originally contained metallic particles of iron and nickel. During heat treatment up to 10008C, metallic particles accompanied the volatile hydrocarbons conducive to forming a filamentous deposit. The deposit obtained demonstrates a semicrystalline material that has an irregular filamentous structure with an average filament diameter of 30 mm. The presence of catalysts after the deposition process was proved in the depositbut catalysts were not found in the residuum.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Fullerrenes, Nanotubes, and Carbon Nanostructures

ISSN

1536-4046

e-ISSN

—

Svazek periodika

2007

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

10

Strana od-do

43-52

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—