Utilization of Photoactive Kaolinite/TiO2 Composite in Cement-Based Building Materials.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27640%2F09%3A00021849" target="_blank" >RIV/61989100:27640/09:00021849 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/26834839:_____/09:#0000027

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Utilization of Photoactive Kaolinite/TiO2 Composite in Cement-Based Building Materials.

Popis výsledku v původním jazyce

Titanium dioxide (TiO2) is the most studied photocatalyst with application potential in many branches of industry. Building industry represent the sector, where the photoactive TiO2 have been already successfully utilized. Concretes, plasters, paints arebuilding materials where the photoactive TiO2 is widely tested. However the amount of TiO2 in these materials is limited with respect to their final properties. If the TiO2 replaces the certain amount of cement in concretes, the resulting compressive strength decreases when this photocatalyst is added in non-adequate content. The surface of kaolinite particles can serve as a matrix for nanosized TiO2 growing what results in photoactive composite ? kaoline/TiO2 formation. After the calcination of this composite the process of kaolinite dehydroxylation is responsible for metakaolinite formation and composite metakaoline/TiO2 with latently hydraulic properties originates. If the metakoline/TiO2 is used for partial cement replacement the c

Název v anglickém jazyce

Utilization of Photoactive Kaolinite/TiO2 Composite in Cement-Based Building Materials.

Popis výsledku anglicky

Titanium dioxide (TiO2) is the most studied photocatalyst with application potential in many branches of industry. Building industry represent the sector, where the photoactive TiO2 have been already successfully utilized. Concretes, plasters, paints arebuilding materials where the photoactive TiO2 is widely tested. However the amount of TiO2 in these materials is limited with respect to their final properties. If the TiO2 replaces the certain amount of cement in concretes, the resulting compressive strength decreases when this photocatalyst is added in non-adequate content. The surface of kaolinite particles can serve as a matrix for nanosized TiO2 growing what results in photoactive composite ? kaoline/TiO2 formation. After the calcination of this composite the process of kaolinite dehydroxylation is responsible for metakaolinite formation and composite metakaoline/TiO2 with latently hydraulic properties originates. If the metakoline/TiO2 is used for partial cement replacement the c

Druh

D - Stať ve sborníku

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/FT-TA4%2F025" target="_blank" >FT-TA4/025: Nanomateriály nové generace a jejich průmyslové aplikace.</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Nanotechnology in Construction 3

ISBN

978-3-642-00979-2

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

—

Název nakladatele

Springer

Místo vydání

Berlin/Heidelberg

Místo konání akce

Praha, Česká republika

Datum konání akce

31. 5. 2009

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—