Microporous Cordierite Ceramics Prepared from Clay Mineral Mixtures Containing Vermiculite

Popis výsledku v původním jazyce

The porous cordierite ceramics were prepared using six clay mineral mixtures of talc, kaolinite and Mg-vermiculite, which has not been used for cordierite synthesis till now. The basic cordierite precursor was mixture consisted of talc, kaolinite and alumina. Other mixtures contained clay minerals and/or alumina with the stoichiometric MgO, SiO2 and Al2O3 ratio close to cordierite, 2MgO-2Al2O3-5SiO2. Ceramic samples contained cordierite enstatite and corundum. Pure cordierite formed from kaolinite nad vermiculite. Vermiculite contributed to the formation of large pores, alumina influenced struts architecture. The porosity of cordierite ceramics was in the range from 46% to 70%. Cordierites showed structural geometry close to the high-temperature hexagonal ?-Mg cordierite.

Název v anglickém jazyce

Microporous Cordierite Ceramics Prepared from Clay Mineral Mixtures Containing Vermiculite

Popis výsledku anglicky

The porous cordierite ceramics were prepared using six clay mineral mixtures of talc, kaolinite and Mg-vermiculite, which has not been used for cordierite synthesis till now. The basic cordierite precursor was mixture consisted of talc, kaolinite and alumina. Other mixtures contained clay minerals and/or alumina with the stoichiometric MgO, SiO2 and Al2O3 ratio close to cordierite, 2MgO-2Al2O3-5SiO2. Ceramic samples contained cordierite enstatite and corundum. Pure cordierite formed from kaolinite nad vermiculite. Vermiculite contributed to the formation of large pores, alumina influenced struts architecture. The porosity of cordierite ceramics was in the range from 46% to 70%. Cordierites showed structural geometry close to the high-temperature hexagonal ?-Mg cordierite.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA205%2F08%2F0869" target="_blank" >GA205/08/0869: Jílové minerály jako hostitelské matrice pro funkční nanostruktury</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Scientific Conference Proceedings

ISSN

1937-6456

e-ISSN

—

Svazek periodika

2

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

4

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—