Preparation and characterization of zirconium-talc for its possible use to the zircon-enstatite ceramic

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27640%2F11%3A86080288" target="_blank" >RIV/61989100:27640/11:86080288 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Preparation and characterization of zirconium-talc for its possible use to the zircon-enstatite ceramic

Popis výsledku v původním jazyce

Effect of milling process in combination with hydrochloric acid treatment on the structure of talc was studied in terms of ability to bind the zirconium in the zirconium-talc composite. Zirconium-talc was prepared from the natural powdered talc from Egypt and aqueous solution of zirconyl chloride. The mechanically and chemically modified talc was investigated by the chemical analysis of elements (XRF), X-ray diffraction (XRD), scanning electron microscopy (SEM) and the measurement of specific surface area (SSA). Combination of procedures of milling with acidification contributed to the increase in SSA of talc from 10.1 to the 17.3 m2/g. The maximum content of zirconium bound in a zirconium-talc was 0.65 wt.%.

Název v anglickém jazyce

Preparation and characterization of zirconium-talc for its possible use to the zircon-enstatite ceramic

Popis výsledku anglicky

Effect of milling process in combination with hydrochloric acid treatment on the structure of talc was studied in terms of ability to bind the zirconium in the zirconium-talc composite. Zirconium-talc was prepared from the natural powdered talc from Egypt and aqueous solution of zirconyl chloride. The mechanically and chemically modified talc was investigated by the chemical analysis of elements (XRF), X-ray diffraction (XRD), scanning electron microscopy (SEM) and the measurement of specific surface area (SSA). Combination of procedures of milling with acidification contributed to the increase in SSA of talc from 10.1 to the 17.3 m2/g. The maximum content of zirconium bound in a zirconium-talc was 0.65 wt.%.

Druh

D - Stať ve sborníku

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

3rd International Conference NANOCON 2011

ISBN

978-80-87294-27-7

ISSN

—

e-ISSN

—

Počet stran výsledku

5

Strana od-do

454-458

Název nakladatele

Tanger

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

21. 9. 2011

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—