Capillary isotachophoresis for separation of silver nanoparticles according to size
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989592%3A15310%2F15%3A33156490" target="_blank" >RIV/61989592:15310/15:33156490 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/61989100:27360/15:86095248 RIV/61989100:27710/15:86095248
Výsledek na webu
<a href="http://pubs.rsc.org/en/content/articlehtml/2015/ra/c5ra10676a" target="_blank" >http://pubs.rsc.org/en/content/articlehtml/2015/ra/c5ra10676a</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1039/c5ra10676a" target="_blank" >10.1039/c5ra10676a</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Capillary isotachophoresis for separation of silver nanoparticles according to size
Popis výsledku v původním jazyce
Capillary isotachophoresis (ITP) was used for the separation of Ag nanoparticles according to their size. For this purpose, ethanol-water dispersions of Ag nanoparticles stabilized by gelatin were prepared. The ITP separations were performed in a column-coupling system filled with two electrolytes with a pH of leading electrolytes of 7.1 (system I - LE: 10 mM HNO3, epsilon-aminocaproic acid, TE: 10 mM caproic acid) and 4.5 (system II - LE: 10 mM HNO3, imidazole, TE: 5 mM 2-(N-morpholino) ethanesulfonicacid). In both electrolyte systems the four main peak-mode zones of Ag nanoparticles migrating at zone boundaries were identified, however, the better separation was achieved by the system II. The Ag nanoparticle dispersions were also examined by dynamiclight scattering (DLS) and transmission electron microscopy (TEM). The zeta potential and thickness of gelatin double layers adsorbed on the nanoparticles were found to depend on pH. The TEM analysis revealed four size fractions of 4 nm,
Název v anglickém jazyce
Capillary isotachophoresis for separation of silver nanoparticles according to size
Popis výsledku anglicky
Capillary isotachophoresis (ITP) was used for the separation of Ag nanoparticles according to their size. For this purpose, ethanol-water dispersions of Ag nanoparticles stabilized by gelatin were prepared. The ITP separations were performed in a column-coupling system filled with two electrolytes with a pH of leading electrolytes of 7.1 (system I - LE: 10 mM HNO3, epsilon-aminocaproic acid, TE: 10 mM caproic acid) and 4.5 (system II - LE: 10 mM HNO3, imidazole, TE: 5 mM 2-(N-morpholino) ethanesulfonicacid). In both electrolyte systems the four main peak-mode zones of Ag nanoparticles migrating at zone boundaries were identified, however, the better separation was achieved by the system II. The Ag nanoparticle dispersions were also examined by dynamiclight scattering (DLS) and transmission electron microscopy (TEM). The zeta potential and thickness of gelatin double layers adsorbed on the nanoparticles were found to depend on pH. The TEM analysis revealed four size fractions of 4 nm,
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CB - Analytická chemie, separace
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/LO1208" target="_blank" >LO1208: Teoretické aspekty energetického zpracování odpadů a ochrany prostředí před negativními dopady</a><br>
Návaznosti
S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
RSC Advances (online)
ISSN
2046-2069
e-ISSN
—
Svazek periodika
5
Číslo periodika v rámci svazku
73
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
6
Strana od-do
59131-59136
Kód UT WoS článku
000357961800022
EID výsledku v databázi Scopus
—